Serratia sp. in the PLA and PCL-supporting biodegradation preparations Serratia sp. jako składnik preparatów wspomagających biodegradację PLA i PCL

10.15199/62.2016.5.9

nr katalogowy: 98493
10.15199/62.2016.5.9

Five Serratia sp. bacterial strains were collected from a water treatment plant and a municipal waste dump and used for studying biodegradn. of polylactide (PLA) and polycaprolactone (PCL) films both under lab. conditions and in the bacteria-vaccinated soil (pot expts.). The tensile strength of the PLA decreased after the treatment. The decompn. of PCL was confirmed by electron microscopy. One of the strains used (Serratia sp. IV-111-4) was particularly active in decompn. of the polymers. This strain had a lower survival rate after lyophilization. Its storage stability was comparable to that of freeze-drying bacteria. The strain can be used as a component of microbiol. prepns. to accelerate degradn. of the polymers. Stwierdzono, że pięć szczepów bakteryjnych z rodzaju Serratia w warunkach in vitro jest zdolnych do wzrostu na foliach wykonanych z polilaktydu (PLA) i polikaprolaktonu (PCL). Obecność bakterii powodowała zmiany w strukturze obu badanych tworzyw, co potwierdzono poprzez analizy z wykorzystaniem skaningowej mikroskopii elektronowej. Jeden ze szczepów Serratia sp. IV-111-4 wyizolowany ze składowiska odpadów w największym stopniu wpływał na przyspieszanie procesu degradacji PLA w warunkach in vitro i in vivo. Stwierdzono osłabienie wytrzymałości PLA na rozciąganie i przyspieszenie procesu rozkładu PCL. Szczep ten charakteryzuje się obniżoną przeżywalnością po procesie liofiliza cji i stabilnością podczas przechowywania w porównaniu z bakteriami nieliofilizowanymi. Potencjalnie Serratia sp. IV-111-4 może być wykorzystana jako składnik preparatów mikrobiologicznych stosowanych do przyspieszania procesu degradacji tworzyw polimerowych. Obecnie rynek tworzyw polimerowych jest w dużej mierze ukierunkowany na "zieloną chemię", przyjazną środowisku naturalnemu, w związku z czym opracowywane są materiały zawierające biodegradowalne tworzywa polimerowe1). Materiały takie pod wpływem temperatury, wilgoci i obecności m[...]

Bibliografia

[1] K. Bajer, H. Kaczmarek, Polimery 2007, 52, nr 1, 13.
[2] A. Gutowska, J. Jóźwicka, S. Sobczak, W. Tomaszewski, K. Sulak, P. Miros, M. Owczarek, M. Szalczyńska, D. Ciechańska, I. Krucińska, Fibres. Text. East. Eur. 2014, 22, nr 5 (107), 99. Fig. 3. Effects of temperature (4°C, 24°C and 30°C) on the survival of freezedried Serratia sp. (IV-111-4) in the subsequent months of storage Rys. 3. Wpływ temperatury (4, 24 i 30°C) na przeżywalność bakterii Serratia sp. IV-111-4 w kolejnych miesiącach przechowywania
[3] K. Hamad, M. Kaseem, F. Deri, Polym. Bull. 2010, 65, 509.
[4] L.T. Lim, R. Auras, M. Rubino, Prog. Polym. Sci. 2008, 33, 820.
[5] R. Malinowski, P. Rytlewski, K. Janczak, A. Raszkowska-Kaczor, K. Moraczewski, M. Stepczyńska, T. Żuk, Polym. Test. 2015, 48, 169.
[6] ISO 14853:2005, Plastics. Determination of the ultimate anaerobic biodegradation of plastic materials in an aqueous system. Method by measurement of biogas production.
[7] V. Massardier-Nageotte, C. Pestre, T. Cruard-Pradet, R. Bayard, Polym. Deg. Stab. 2006, 91, 620.
[8] P.K. Shin, M.H. Kim, J.M. Kim, J. Environ. Polym. Degrad. 1997, 5, 33.
[9] L. Husárová, S. Pekărová, P. Stloukal, P. Kucharzcyk, V. Verney, S. Commereuc, A. Ramone, M. Koutny, Int. J. Biol. Macromol. 2014, 71, 155.
[10] P. Stloukal, A. Kalendova, H. Mattausch, S. Laske, C. Holzer, M. Koutny, Polym. Test. 2015, 41, 124.
[11] B. Kołwzan, W. Adamiak, K. Grabas, A. Pawełczyk, Podstawy mikrobiologii w ochronie środowiska, Wrocław 2005, 31.
[12] G. Dąbrowska, K. Hrynkiewicz, K. Kłosowska, A. Goc, Ochr. Środ. 2011, 33, nr 2, 53.
[13] K. Janczak, G. Dąbrowska, Z. Znajewska, K. Hrynkiewicz, Przem. Chem. 2014, 93, nr 12, 2218.
[14] K. Janczak, G. Dąbrowska, Z. Znajewska, K. Hrynkiewicz, Przem. Chem. 2014, 93, nr 12, 2222.
[15] K. Janczak, G. Dąbrowska, K. Hrynkiewicz,
[w:] Mikroorganizmy - roślina - środowisko w warunkach zmieniającego się klimatu, Puławy-Lublin 2013, 138.
[16] K. Janczak, G. Dąbrowska, K. Hrynkiewicz,
[w:] Protection of soil functions. Challenges for the future, Wydawnictwo IUNG, Puławy 2013, 151.
[17] K. Janczak, G. Dąbrowska, K. Hrynkiewicz, A. Raszkowska-Kaczor, A. Richert,
[w:] Mikrobiologia a ochrona środowiska, Wydawnictwo SGGW, Warszawa 2014, 55.
[18] K. Janczak, G. Dąbrowska, K. Hrynkiewicz, A. Raszkowska-Kaczor,
[w:] mikrobiologia a ochrona środowiska, Wydawnictwo SGGW, Warszawa 2014, 56.
[19] K. Janczak, Z. Znajewska, G. Dąbrowska, K. Hrynkiewicz, A. Richert,
[w:] Transformacja zanieczyszczeń w glebie, Wydawnictwo AGH, Kraków 2014, 63.
[20] PN-EN ISO 846:2002, Tworzywa sztuczne. Ocena działania mikroorganizmów.
[21] PN-EN ISO 527:1998, Tworzywa sztuczne. Oznaczanie właściwości mechanicznych przy statycznym rozciąganiu.

Zeszyt


PRZEMYSŁ CHEMICZNY - e-zeszyt (pdf) 2016-5 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEMYSŁ CHEMICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEMYSŁ CHEMICZNY - prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEMYSŁ CHEMICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Open Access

Zeszyt

2016-5

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma