The influence of iron and molybdenum on the corrosion process of protective ternary Zn-Fe-Mo alloy coatings in chloride solution

10.15199/40.2016.4.2

nr katalogowy: 97709
10.15199/40.2016.4.2

The structure and chemical composition of corrosion products of Zn coating, binary Zn-Fe(1.7% at. Fe) and ternary Zn-Fe- Mo (6.6% at. Fe, 1.9% at. Mo) alloy coatings after 24 hours exposure in 0.5 mol·dm-3 solution of NaCl were investigated. It was established that the presence of iron and molybdenum in the zinc alloy coating has a positive impact on the protective properties of the coatings and on the homogeneity of the layer of corrosion products. X-ray diffraction analysis of coatings revealed the presence of: zinc oxide, zinc hydroxide, zinc hydroxide carbonate and zinc hydroxide chloride. Moreover, the corrosion products are almost the same for all tested coatings, regardless of the fact that corrosion potentials of these coatings vary considerably. The ternary Zn-Fe-Mo coating exhibits the highest corrosion resistance among all investigated coatings during 24 h immersion. Keywords: Zn-Fe-Mo coating, electroplating; zinc corrosion, XRD, SEM Wpływ żelaza i molibdenu na proces korozji ochronnych trójskładnikowych powłok stopowych Zn-Fe-Mo w środowisku chlorkowym W artykule opisano wyniki badań struktury i składu chemicznego warstw produktów korozji wytworzonych na powierzchni powłok: Zn, dwuskładnikowej Zn-Fe (1,7% at. Fe) oraz trójskładnikowej Zn-Fe-Mo (6,6% at. Fe, 1,9% at. Mo) po 24 godzinach ekspozycji w 0,5 mol·dm-3 roztworze NaCl. Wykazano, że obecność żelaza i molibdenu w cynkowej powłoce stopowej ma pozytywny wpływ na jej właściwości ochronne oraz na jednorodność powstającej warstwy produktów korozji. Analiza rentgenowska wskazała jednoznacznie na: tlenek cynku, wodorotlenek cynku, hydroksywęglan cynku oraz hydroksychlorek cynku, jako główne produkty korozji badanych powłok w wodnym roztworze NaCl. Niezależnie od znacznych różnic w zmierzonych potencjałach korozji poszczególnych powłok, skład jakościowy produktów korozji był zbliżony, a najwyższą odpornością na korozję w ciągu 24 godzin ekspozycji charakteryzowała się [...]

Bibliografia

[1] Boshkov N., K. Petrov, S. Vitkova, S. Nemska, G. Raichevsky. 2002. "Composition of the corrosion products of galvanic alloys Zn-Co and their influence on the protective ability". Surface and Coatings Technology 157 (2-3): 171-178.
[2] Bučko M., J. Rogan, S.I. Stevanović, A. Perić-Grujić, J.B. Bajat. 2011. "Initial corrosion protection of Zn-Mn alloys electrodeposited from alkaline solution". Corrosion Science 53 (9) : 2861-2871.
[3] Hamlaoui Y., L. Tifouti, F. Pedraza. 2010. "On the corrosion resistance of porous electroplated zinc coatings in different corrosive media". Corrosion Science 52, (6) : 1883-1888.
[4] Szczygieł Bogdan, Agnieszka Laszczyńska, Włodzimierz Tylus. 2010. "Influence of molybdenum on properties of Zn-Ni and Zn-Co alloy coatings". Surface and Coatings Technology 204 (9-10) : 1438-1444.
[5] Winiarski Juliusz, Bogdan Szczygieł. 2015. "The effect of plating bath pH on the properties of protective ternary Zn-Fe-Mo alloy coatings deposited from citrate-sulphate solution". Ochrona Przed Korozją 58 (4) : 99-102.
[6] Winiarski Juliusz, Włodzimierz Tylus, Bogdan Szczygieł. 2016. "EIS and XPS investigations on the corrosion mechanism of ternary Zn-Co-Mo alloy coatings in NaCl solution". Applied Surface Science 364 : 455-466.
[7] Winiarski Juliusz, Włodzimierz Tylus, Katarzyna Winiarska, Bogdan Szczygieł. 2015. "The influence of molybdenum on the corrosion resistance of ternary Zn-Co-Mo alloy coatings deposited from citrate-sulphate bath". Corrosion Science 91 : 330-340.
[8] Zhang X.G. 1996. Corrosion and Electrochemistry of Zinc. New York: Plenum Press.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 97709 "The influence of iron and..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2016-4 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2016-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma