Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2016 - zeszyt 1

Characteristic of cyclic oxidation of chosen austenitic steels in a steam atmosphere

10.15199/40.2016.1.1

nr katalogowy: 96104
10.15199/40.2016.1.1

The aim of the study was to evaluate the oxidation resistance of chromium-nickel austenitic steels in an atmosphere, which contains oxygen and steam at a temperature of 750oC. The oxidation test of steel samples X2CrNiMo17-12-2, X6CrNiMoTi17- 12-2, Super 304H and HR3C was carried out in a cyclic mode, made up of 100 cycles trials of 2 hours. The results show the mass changes of steels caused by a cyclic oxidation. The morphology and chemical composition of the oxide layer formed on the surface of tested samples were also described. It has been proved that under these conditions HR3C steel shows the best heat resistance and X2CrNiMo17-12-2 steel presents the worst tendency of oxides to defoliation. Keywords: austenitic steels, cyclic oxidation, steam Charakterystyka cyklicznego utleniania w parze wodnej wybranych stali austenitycznych Celem badań była ocena odporności na utlenianie austenitycznych stali chromowo-niklowych w atmosferze zawierającej tlen i parę wodną w temperaturze 750oC. Utlenianie próbek ze stali X2CrNiMo17-12-2, X6CrNiMoTi17-12-2, Super 304H i HR3C przeprowadzono w sposób cykliczny, składający się ze 100 cykli trwających 2 godziny. Przedstawiono wyniki zmiany masy materiałów wywołanych cyklicznym utlenianiem. Scharakteryzowano również morfologię i skład chemiczny warstw tlenkowych powstałych na powierzchni badanych stali. Wykazano, że najlepszą żaroodporność w tych warunkach posiada stal HR3C, a najgorszą stal X2CrNiMo17-12-2 wykazująca skłonność do defoliacji tlenków. Słowa kluczowe: stale austenityczne, utlenianie cykliczne, para wodna 1. Introduction Domestic energy sector is outdated and contains many power plants, which are characterized by low efficiency of power units, large increase of their failure and being below the standards of NOx, SO2 and CO2 emission [2]. Development of national energy is heading towards increasing the productivity, efficiency and significant reduction of emissions of harmful substances[...]

Bibliografia

[1] Baker B.A., R.D. Gollihue and J.J. de Barbadillo. 2012. "Fabrication and heat treatment of weld joints in Inconel Alloy 740H™ superalloy steam headers pipe and superheater tubing". Welding and Repair Technology for Power Plants, 10th Int. EPRI Conference, Floryda, USA.
[2] Coleman K., R. Viswanathan, J. Shingledecker, JH. Sarver and others. 2003. "Boiler materials for ultrasupercritical coal power plants". First Quarterly Report October 1 - December 31, U.S. DOE NO.: DE-FG26- 01NT41175.
[3] Evans N.D., P.J. Maziasz, R.W. Swindeman, G.D. Smith. 2004. "Microstructure and phase stability in Inconel 740 during creep". Scripta mater. 51 : 503-507.
[4] Hwang T.Y., R. Banerjee, J. Tiley, R. Srinivasan, G.B. Visvanathan, H. Fraser. 2009. Metall. Mater. Trans, A40 : 24-35.
[5] Sanders J., J. Ramirez, B. Baker. 2007. "Weldability of Inconel 740 for USC Boiler Applications". 5th Int. Conf. on Advances in Mater. Technol. for Fosil Power Plants, EPRI, Floryda, USA.
[6] Shingledecker J.P., R.W. Swindeman, Q. Wu and V.K. Vasudevan. 2005. "Creep Strength of High-Temperature Alloys for USC Steam Boilers". Proc. to the 4th Int. Conf. on Adv. in Mat. Technol. for Fossil Power Plants (Hilton Head, SC, Oct. 25-28, 2004), ASM-International, Materials Park, OH, 2005.
[7] Smith G.D., H.W. Sizek. "Introduction of an Advanced Superheater Alloy for Coal-Fired Boilers". Corrosion 2000, Paper 00256 © 2000 NACE International, TX.
[8] Yan Ch., L. Zhendong, A. Godfrey, L. Wei, W Yuqing. 2014. "Microstructure evolution and mechanical properties of Inconel 740H during aging at 750oC". Mater. Sc. & Eng. A589 : 153-164.
[9] Zhao S., X. Xie, G.D. Smith, J. Patel. 2003. "Microstructural stability and mechanical properties of a new nickel-based superalloys". Mater. Sc & Eng. A355 : 96-105.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 96104 "Characteristic of cyclic ..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2016-1 licencja: Osobista Produkt cyfrowy	42.00 zł
OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2016-10 licencja: Osobista Produkt cyfrowy	42.00 zł
OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2016-11 licencja: Osobista Produkt cyfrowy	42.00 zł
OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2016-12 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2016-1

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma