Czasopismo | PRZEGLĄD ELEKTROTECHNICZNY | Rocznik 2016 - zeszyt 1

Magnetic properties of La0.7Sr0.3Mn0.85Nb0.15-xMgxO3 system

10.15199/48.2016.01.36

nr katalogowy: 96022
10.15199/48.2016.01.36

Structural and magnetization measurements have been performed on the La0.7Sr0.3Mn0.85Nb5+ 0.15-xMg2+ xO3 system. With rise of the Mg2+ content the formal oxidation state manganese increases from +3 (x=0) up to +3.55 (x=0.15). The substitution of Nb5+ with Mg2+ leads to a gradual weakening of the ferromagnetic component while in the x=0.15 compound A-type antiferromagnetic short-range order is stabilized in spite of macroscopic R-3c symmetry. It is suggested that ferromagnetism is originated from superexchange interactions via oxygen. Streszczenie. Przeprowadzono pomiary strukturalne i namagnesowania układu La0.7Sr0.3Mn0.85Nb5+ 0.15-xMg2+ xO3.Wraz ze wzrostem zawartości Mg2+formalny stopień utlenienia manganu wzrasta z +3 (x=0) aż do +3.55 (x=0.15). Zastąpienie Nb5+ poprzez Mg2+prowadzi do stopniowego osłabienia składnika ferromagnetycznego podczas gdy w związku x=0.15 typu A antyferromagnetyczny porządek krótkiego zasięgu jest ustabilizowany pomimo makroskopowej symetrii R-3c. Sugeruje się, że ferromagnetyzm pochodzi z nadwymiany za pomocą tlenu. (Magnetyczne właściwości układu La0.7Sr0.3Mn0.85Nb0.15-xMgxO3). Keywords: magnetization measurements, ferromagnetism, superexchange interactions. Słowa kluczowe: pomiary namagnesowania, ferromagnetyzm, nadwymiana. Introduction La1-xAxMnO3 (A=Ca, Sr, Ba) manganites have been of interest for many years since they exhibit very intriguing magnetic and magnetotransport properties [1-3]. In order to explain the interplay between magnetic and transport properties Zener introduced a special form of exchange interactions through charge carriers - double exchange [2]. De Gennes [4] developed a theory of double exchange and predicted that a canted magnetic structure forms at intermediate concentrations between the antiferromagnetic and ferromagnetic states. However, nuclear magnetic resonance data strongly support the mixed phase scenario as two different hyperfine lines corresponding to ferromagn[...]

Bibliografia

[1] Dagotto E., Hotta T., Moreo A., Colossal magnetoresistant materials: the key role of phase separation, Physics Reports, 344 (2001), No. 1-3, 1-153
[2] Zener C., Interaction between the d-shells in the transition metals. II. Ferromagnetic compounds of manganese with perovskite structure, Phys. Rev., 82 (1951), No. 3, 403-405
[3] Şen C., Alvarez G., Dagotto E., Competing ferromagnetic and charge-ordered states in models for manganites: the origin of the colossal magnetoresistance effect, Phys. Rev. Lett., 98 (2007), No. 12, 127202-1-4
[4] De Gennes P. G., Effects of double exchange in magnetic crystals, Phys. Rev., 118 (1960), No. 1, 141-154
[5] Allodi G., De Renzi R., Guidi G., Licci F., Pieper M.W., Electronic phase separation in lanthanum manganites: evidence from 55Mn NMR, Phys. Rev. B, 56 (1997), No. 10, 6036-6046
[6] Kumagai K., Iwai A., Tomioka Y., Kuwahara H., Tokura Y., Yakubovskii A., Microscopically homogeneous magnetic structure of La1-xSrxMnO3 beyond the range of 0[7] Choi K.-Y., Zhou H.D., Kuhns P.L., Reyes A.P., Dalal N.S., Physica B, 405 (2010), No. 1, 390-393
[8] Roisnel T., Rodrıquez-Carvajal J., Winplotr: a windows tool for powder diffraction pattern analysis, J. Mater. Sci. Forum, 378- 381 (2001), 118-123
[9] Zhou J.-S., Goodenough J.B., Orbital mixing and ferromagnetism in LaMn1-xGaxO3, Phys. Rev. B, 77 (2008), No.17, 172409-1-4
[10] Deisenhofer J., Paraskevopoulos M., Krug von Nidda H.-A., Loidl A., Interplay of superexchange and orbital degeneracy in Cr-doped LaMnO3, Phys. Rev. B, 66 (2002), No.5, 054414-1-7
[11] Zhou J.-S., Goodenough J.B., Paramagnetic phase in singlecrystal LaMnO3, Phys. Rev. B, 60 (1999), No. 22, R15002- R15004
[12] Goodenough J.B., Magnetism and Chemical Bond, Interscience, New York/London, 1963.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 96022 "Magnetic properties of La..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2016-1 licencja: Osobista Produkt cyfrowy	55.00 zł
PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2016-10 licencja: Osobista Produkt cyfrowy	55.00 zł
PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2016-11 licencja: Osobista Produkt cyfrowy	55.00 zł
PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2016-12 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEGLĄD ELEKTROTECHNICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEGLĄD ELEKTROTECHNICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Zeszyt

2016-1

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma