Wpływ ciśnienia prasowania na właściwości kompozytów WCCo-cBN wytwarzanych metodą PPS

10.15199/28.2015.6.34

nr katalogowy: 95637
10.15199/28.2015.6.34

Influence of load on the properties of WCCo-cBN composites produced by the PPS method Cubic boron nitride (cBN) is the material next to diamond in respect of hardness and heat conductivity, but, contrary to diamond, it shows weak reactivity with ferrous materials. In view of these properties, cubic boron nitride is an excellent material for the fabrication of cutting tools such as e.g. those made of heat-treated steels, nickel-based alloys, or cobalt. Under elevated temperature and under normal pressure, cubic boron nitride undergoes transformation into its stable phase hBN. Traditional cBN sinters (polycrystalline cubic boron nitride — PCBN) with a metallic matrix are usually sintered using the expensive High Pressure High Temperature (HPHT) method which requires high pressure of 4÷5 GPa to avoid the transformation of hard cBN into its soft hexagonal hBN phase. The present study is concerned with how the load affect on the properties of the WCCo composites which contain 20 vol. % of cBN with the particle size ranging from 5 to 12 μm. The powders were sintered in an apparatus for high-current pulse sintering (Pulse Plasma Sintering). The idea underlying the process is to heat the pre-consolidated powder using electric pulses, the heating being realized via the Joule heat dissipated at the contacts between the individual powder particles. During the electric current impulses the instantaneous temperature on the powder particle surfaces reaches several thousand Celsius degrees, and after the current decays, it quickly falls to the prescribed sintering temperature. The study showed that the sintering at the temperature 1100°C, under the load 30 MPa (in the first stage) and 100 MPa (in the second stage), for 10 min yielded sinters with the density above 99% GT with hardness of about 223 HV10. Key words: pulse plasma sintering, cubic boron nitride (cBN), cemented carbides, composites. Regularny azotek boru (cBN) jest drugim po diamencie[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 95637 "Wpływ ciśnienia prasowani..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2015-6 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2015-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma