Analiza właściwości tribologicznych powłok a-C:H:SiOx wytwarzanych metodą RF PACVD

10.15199/28.2015.6.25

nr katalogowy: 95628
10.15199/28.2015.6.25

Analysis of tribological properties of a-C:H:SiOx coatings synthesized by RF PACVD method SiOx incorporated carbon coatings were synthesized using RF PACVD (Radio Frequency Plasma Assisted Chemical Vapour Deposition) method with use of mixture of methane (CH4) and hexamethylodisiloxane (HMDSO). The processes of synthesis were conducted using different CH4/HMDSO flow ratios and wide range of the self-bias potential of the r.f. electrode. As the substrate oxidized Ti6Al7Nb titanium alloy was used. Friction coefficient and wear resistance analysis was performed using the T-11 tribometer in the ball-on-disc configuration and counterpart made of 100Cr6 steel. Wear track analysis was made using scanning electron microscopy and Raman spectroscopy. The resistance against wear was determined basing on the registered wear profiles and scars on the surface of the coatings and the balls respectively. The results of the conducted examinations prove the varied impact of the process parameters on the tribological properties of the obtained coatings. A noticeably positive influence of SiOx incorporation on the decreasing value of the coefficient of friction was registered for as low concentration of silicon as 0.5 at. %. Nevertheless for low self-bias potentials coatings with high concentration of silicon and oxygen were damaged just after few meters of the sliding distance. The main wear mechanism of a-C:H:SiOx coatings is the third body effect. It seems that incorporation of SiOx into carbon coatings limits the graphitisation phenomena, which lead to formation of the transition layer acting as the solid lubricant. Despite significantly lower and stable coefficients of friction of a-C:H:SiOx coatings with higher concentrations of silicon and oxygen they do not provide sufficient protection against wear of the co-working elements. Key words: DLC, SiOx incorporation, friction, wear. Domieszkowane SiOx powłoki węglowe zostały wytworzone metodą RF PACVD (Radio [...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 95628 "Analiza właściwości tribo..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2015-6 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2015-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma