Structure and properties of Inconel 625 and 686 weld overlays deposited onto boiler pipes and membrane walls by the CMT technique In the paper results of complex microstructural, microchemical, mechanical and corrosion resistance investigations of Inconel 625 and 686 weld overlays deposited onto boiler pipes and membrane walls, which are used within boilers for waste incineration, are described. The membrane walls and boiler pipes (made of 16Mo3 steel) were weld overlaid in the SEFAKO S.A. using CMT (Cold Metal Transfer) technique. The average thickness of weld deposited coatings was about 2.5 mm, while thickness of the heat affected zone in pipes about 0.6 mm. The microstructure and chemical composition of the deposited coatings were analyzed using light, scanning and transmission electron microscopes connected to an energy dispersive X-ray analyzer (EDS) apparatus. The chemical composition variations in the content of Ni, Fe, Cr, Mo and Nb in the direction perpendicular to the coatings surface and dendritic microsegregation were examined. Moreover, mechanical properties were determined using tensile test samples made of overlaid pipes and membrane walls. Examinations showed a high strength and plasticity of the Inconel 625 and 686 weld overlaid boiler pips and membrane walls. EDS Microprobe measurements of the Inconel 625 and 686 weld overlays showed the Fe content rapidly decreasing in the direction from the Fe-rich substrate towards the coating to the level of 5 wt % within 30 μm, and near the coating surface the Fe content reaches level of only about 3%. Research showed that due to microsegregation that occurs during the process of solidification of the Inconel 625 weld overlays, the cores of the dendrites are richer in Ni, Fe and Cr, while the areas between dendrite arms, the so-called interdendritic regions, are richer in Mo and Nb. It was shown that W in 686 alloy segregates much less than Nb in Inconel 625 coatings. Microstructu[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 95605 "Struktura i właściwości p..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2015-6 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2015-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma