Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2015 - zeszyt 4

Wpływ obróbki wstępnej i koncentracji propanu w mieszaninie z amoniakiem na wyniki węgloazotowania fluidalnego niskowęglowych stali typu C25 i S355

10.15199/28.2015.4.7

nr katalogowy: 94600
10.15199/28.2015.4.7

The effect of pretreatment and propane concentration in the mixture with ammonia on the results of the fluidized bed nitrocarburizing of low carbon C25 and S355 steels The subject of this study was to investigate the effect of pretreatment before fluidized bed nitrocarburizing process and the amount of the carbon carrier addition in the form of propane on the hardness, microstructure and compounds layer and diffusion zone thicknesse in the case of low-carbon structural steel type C25 and S355. Constant process time 4 h and temperature 580°C were assumed. Pretreatments consisted of samples oxidation at temperature 350°C for 30 minutes or short-lasting nitriding in the ammonia at temperature 480°C for 25 minutes and removing the samples from the fluidized bed to the air in order to oxidize them. Both variants were compared with samples without pretreatment. The hardness measurements on the surface of nitrocarburized samples were made at three loads 0.1, 0.5 and 1 kG in order to capture the differences in the microstructure and thickness of the hardened layers. The results of measurements with load of 0.1 kG show the characteristic of the thin subsurface zone 2÷3 μm, in which major changes take place, caused by the nitrocarburizing environment, core diffusion of alloying elements and impurities, as well as geometric surface conditions and pre-machining treatment. The results of measurements with load of 0.5 and 1 kG are dependent mainly on the nitrocarburized layer thickness and substrate hardness. In the assumed process conditions there was not found, with certain exceptions, significant effect of studied factors on layer thickness, however they have significant impact on the hardness HV0.1, HV0.5 and HV1 measured on the surface of nitrocarburized samples. In order to obtain the highest possible hardness and layers uniformity - lower porosity, a 2% propane addition to the ammonia was favourable. In studies it was found, that due to th[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 94600 "Wpływ obróbki wstępnej i ..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2015-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2015-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma