EFFECT OF SECONDARY CARBIDES PRECIPITATED IN WIDMANSTATTEN SHAPE ON TRIBOLOGICAL PROPERTIES OF CAST MATERIALS

10.15 199/67.2015.7.4

nr katalogowy: 92510
10.15 199/67.2015.7.4

Hypereutectoid cast iron alloys such as G200CrNiMo4-3-3 have a very complex microstructure. The microstructure of these alloys is transformed ledeburite, perlite and secondary carbides precipitates. Proeutectoid carbides can precipitate in different morphologies and areas such as grain boundary precipitates, intergranular precipitates and Widmanstatten shape. Usually Widmanstatten microstructure is treated as a negative microstructural component, because of the possibility of stress concentration on the top of Widmanstatten carbides needles which adversely affect on material properties such as tensile strength and fracture toughness. Tribological measurements show a certain correlation between the amount of Widmanstatten carbides and friction coefficient of the material. Tests presented in this work were performed by the use of T05 block-on ring tribological tester. Various times and loads were used during tests. In addition a pin on disc tests in 750 °C were performed. Two variants of heat treatment, designed to changing the volume fraction and shape of secondary carbides precipitated in Widmanstatten shape, were used. It has been shown that the friction coefficient, increases with a volume fraction and average surface area of Widmanstatten carbides precipitations. Caused by the heat treatment changes in shape of Widmannstatten cementite precipitations results in a decrease in average friction coefficient. Keywords: friction coefficient, cast steel, proeutectoid cementite, Widmanstatten microstructure WPŁYW WYDZIELEŃ CEMENTYTU W UKŁADZIE WIDMANSTATTENA NA WŁASNOŚCI TRIBOLOGICZNE MATERIAŁÓW ODLEWANYCH Nadeutektyczne odlewane stopy żelaza, takie jak staliwo G200CrNiMo4-3-3 mają bardzo złożoną mikrostrukturę, składającą się z ledeburytu przemienionego, perlitu i wydzieleń węglików drugorzędowych. Węgliki drugorzędowe mogą wydzielać się w różnych miejscach i morfologiach, takich jak: wydzielenia na granicach ziarn, w układzie Widmanstattena o[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 92510 "EFFECT OF SECONDARY CARBI..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


RUDY I METALE NIEŻELAZNE - e-zeszyt (pdf) 2015-7 licencja: Osobista Produkt cyfrowy	32.00 zł

Zeszyt

2015-7

Twój Koszyk

Publikacja

Zeszyt

Zeszyt

Czasopisma