EFFECT OF PLASTIC DEFORMATION ON THE MICROSTRUCTURE, SIZE AND DISTRIBUTION OF SiC REINFORCING PARTICLES IN THE CAST F3K.10S COMPOSITE

10.15 199/67.2015.7.3

PAWEŁ KURTYKA

nr katalogowy: 92509
10.15 199/67.2015.7.3

The aim of this investigation was to comparison of microstructure changes of SiC reinforcing particles after plastic deformation process, in the cast composite F3K.10S. Aluminum matrix reinforced with 10 % vol. SiC particles was modified using friction stir processing method. Changing of distribution of the reinforcement particles was calculated and analyzed using new Mityushev’s RVE theory with Eisenstein-Rayleigh sums (M-sum) and PointSel software. The mechanical properties were determined on the hardness tests. The significant changes in the concentration, distribution and size of SiC particles were observed. Hardness testing of selected modified areas showed significant differences in the HV01 value in thermomechanical hardening areas. The resulting increase in hardness exceeded 30 %, but the obtained values of standard deviation have indicated that, despite a homogenized distribution of the reinforcing particles and their fragmentation, significant variations between individual measurements still persisted in the modified material. The processed material shows a considerable decrease in the average size of the reinforcing particles, i.e. from the initial area of 60÷70 square microns to a value below 20 square microns. It is believed that the obtained results should contribute to process optimization and a better understanding of the phenomena that occur during FSP modification. Keywords: cast metal matrix composites, friction stir processing, new RVE theory WPŁYW DEFORMACJI PLASTYCZNEJ NA MIKROSTRUKTURĘ, WIELKOŚĆ I ROZKŁAD FAZY WZMACNIAJĄCEJ SiC W ODLEWANYM KOMPOZYCIE F3K.10S Celem badań było porównanie zmian mikrostruktury cząstek wzmacniających SiC po procesie deformacji plastycznej odlewanego kompozytu F3K.10S. Kompozyt o osnowie aluminiowej wzmocnionej 10 % obj. cząstek SiC został zmodyfikowany metodą FSP. Zmianę rozkładu cząstek wzmacniających obliczono i analizowano za pomocą nowej teorii RVE Mityusheva z pomocą sum Eise[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 92509 "EFFECT OF PLASTIC DEFORMA..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


RUDY I METALE NIEŻELAZNE - e-zeszyt (pdf) 2015-7 licencja: Osobista Produkt cyfrowy	32.00 zł

Zeszyt

2015-7

Twój Koszyk

Publikacja

Zeszyt

Zeszyt

Czasopisma