THE PROPERTIES AND MICROSTRUCTURE OF AlTi6/Al2O3 JOINTS

10.15199/67.2015.4.1

nr katalogowy: 90835
10.15199/67.2015.4.1

The influence of the titanium addition into aluminium on the bond strength properties and structure of interface of the AlTi6/Al2O3 joints was investigated. The bond strength of the metal/Al2O3 joints was determined by the push-off test. Addition of 5.9 wt.%. Ti to Al caused the reduction of shear strength of the AlTi6/Al2O3 joints. The investigations by mean of electron microscopy equipped with a spectrometric system for microanalysis of the chemical composition revealed TiAl3 phases formed at the AlTi6/Al2O3 interface. Oxygen was detected in some areas of TiAl3 phases. Finally, this structure of the AlTi6/Al2O3 interface was responsible for lower bond strength comparing to properties of the Al/Al2O3 joints. Keywords: AlTi6/Al2O3 joint; shear strength, interface WŁAŚCIWOŚCI I MIKROSTRUKTURA POŁĄCZENIA AlTi6/Al2O3 W pracy przedstawiono badania dotyczące wpływu dodatku tytanu do aluminium na wytrzymałość na ścinanie oraz mikrostrukturę połączenia AlTi6/Al2O3. Wyniki wykazały, że dodanie tytanu do aluminium wpływa na obniżenie wytrzymałość na ścinanie badanego połączenia. Badania mikrostrukturalne (SEM oraz TEM) połączone z analizą składu chemicznego wykazały powstanie wydzieleń fazy TiAl3 na granicy rozdziału połączenia. W obszarach fazy TiAl3 obserwowano obecność tlenu. Tworzenie nowych faz na granicy rozdziału połączenie AlTi6/Al2O3 odpowiada za obniżenie wytrzymałości w porównaniu z połączeniem Al/Al2O3. Słowa kluczowe: połączenie AlTi6/Al2O3 joint; wytrzymałość na ścinanie, granica rozdziału Introduction The basis of the technological processes such as soldering, brazing and production of metal matrix composite materials is the assurance of the appropriate wettability of ceramic by liquid metals and receiving the stable joint between the metal and ceramic. Therefore, the wetting of the Al2O3 by liquid aluminium has been investigated by several authors using the sessile drop method [1÷5]. These studies concentrated mainly on the in[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 90835 "THE PROPERTIES AND MICROS..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


RUDY I METALE NIEŻELAZNE - e-zeszyt (pdf) 2015-4 licencja: Osobista Produkt cyfrowy	32.00 zł

Zeszyt

2015-4

Twój Koszyk

Publikacja

Zeszyt

Zeszyt

Czasopisma