Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2014 - zeszyt 2

Study of the surface layers of 18G2A steel after plasma surfacing with WC and Fe-Cr powders

nr katalogowy: 84299

Surfacing technology allows for production of surface layers on any materials, on products of any chemical and phase composition, and any shape. Rods or powders made of ceramics, metals, cermets or plastics may be used as surfacing materials. This method is used to produce surface layers with special properties, such as wear and corrosion resistance, refractoriness and creep resistance [1÷7]. Plasma surfacing method consists of melting additional material (in the form of bulk or powder) along with substrate in plasma arc at temperatures of about 15 000÷20 000°C. Additional material and melted metalic substrate create a weld overlay in which substrate participation can reach tens of percent. Mechanical finishing is not necessary because weld overlays are homogeneous, and their faces are smooth [2, 5]. High hardness (WC - 2240 HV, B4C - 2800 HV), wear resistance as well as corrosion and oxidation resistance are the major advantages of carbides. Another important advantage is the high strength to density ratio as well as the high melting point (above 2000°C) [1, 5, 7]. The aim of this study was to determine microstructure, thickness, hardness and chemical composition of the surface layers produced on 18G2A steel by plasma surfacing. EXPERIMENTAL DETAILS The surface layers were produced using WC and Fe-Cr powders. The four different powder mixtures were used, and their percentage compositions are shown in Table 1. The rectangular specimens (width of 30 mm, length of 50 mm and height of 10 mm) were used for the study. The tungsten carbide used in the study was in the form of irregular crystals with sharp edges, and their size ranged fro[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 84299 "Study of the surface laye..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2014-2 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2014-2

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma