Influence of solution heat treatment on the microstructure and hardness of the Ni-Ta-Al alloy with a high carbon content

PIOTR BAŁA

nr katalogowy: 84275

The microstructure and properties of tools have strong influence on their throughput and reliability what favours development of mechanization and automate of technological lines. An increased interest in the production of machine element made of advanced materials (such as high alloyed steels or titanium alloys) forces the development of tool materials being formed at high temperature. Steels are a typical material for tool production. For high temperature application hot-work and high speed steels are applied [1÷5]. The hot work steels containing from 0.3 to 0.6% C, up to 5% Cr and Mo, W and V are universally applied as tool materials for operations at high temperature. Usually, the most important property of the steel is high impact resistant, which is required to crack resistant. Therefore their microstructure does not include primary or secondary carbides. Tools made of these steels obtain functional qualities by toughening, i.e. combined quenching with medium or high tempering. Tempering of tool steels usually takes place in the temperature range: 550÷620°C. Strengthening is achieved by precipitation of alloy carbides of MC and M2C (V, Mo and W) type [1, 2]. Several tools have to operate at temperature above 600°C, sometimes even at 1000°C, at which quenched and tempered steels soften, causing rapid decrease in a lifetime of tools. A development of high temperature creep-resisting nickelbased alloys relied mainly on the modification of 80% Ni and 20% Cr alloy known for its good creep-resistance. On account of ineffectiveness of strengthening by carbides in high temperature, a hardening of Ni-based alloys was obtained by the intermetallic phase Ni3(Ti, Al), designated as [...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 84275 "Influence of solution hea..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2014-2 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2014-2

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma