The effect of diffusion treatment of double (Al/Zr and Zr/Al) coatings on the microstructure of the system coating/Ni substrate

nr katalogowy: 79743

The improvement of engine turbines efficiency is achieved by the use of effective cooling system of turbine blades and by deposition of diffusion-type protective coatings on nickel based superalloys [1÷5]. Aluminide coatings deposited on nickel-based superalloys provide a good oxidation and corrosion resistance of blades. Addition of small amount of reactive elements such as Zr, Hf, Y, or Ce to the NiAl coatings has beneficial effects on the oxidation behaviour. These beneficial effects include improvement in adhesion of alumina scales and reduction of oxide scale growth rate [6, 7]. Zirconium co-deposited with aluminum on the nickel superalloy by the CVD process was developed by ONERA “National Research and Scientific Institute for Outer Space" and SNECMA “National Company for the Design and Construction of Aviation Engines". Zirconium provided by the ZrCl2,8H2O activator [8] is located far below the coating surface, at the interface between the -NiAl coating and the interdiffusion zone. This interface corresponds to the initial surface of the superalloy and zirconium deposition occurs at the beginning of the process. The interdiffusion zone consists of the -NiAl matrix and phases containing additional elements from the superalloy (Cr, Co, W, Al, Ti, Mo) [8]. During oxidation zirconium migrates towards the surface and the Zr distribution becomes homogeneous in the whole oxide layer. Zirconium may migrate via NiAl grain boundaries, where it is known to segregate [9]. Thus, Zr present in the oxide, can be expected to modify the stress relief by reducing the oxide creep rate. Zirconium delays the oxide scale spalling and inhibits the formation of cavities at the metal/oxide interface and there is no voiding at the metal/oxide interface, unlike in Pt-modified NiAl coatings [8]. The absence of voiding in the presence of Zr is expected to improve alumina adhesion on the nickel aluminite. Several techniq[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 79743 "The effect of diffusion t..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma