Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2013 - zeszyt 4

Structural characterization of surface layers in sintered DistaloyAE and DistaloyHP

nr katalogowy: 79736

The beneficial feature of diffraction methods is their non-destructive character and a large number of structural information contained in diffraction pattern. The classical Bragg-Brentano (B-B) and the Grazing Incidence Diffraction (GID) methods were utilized in this investigation. Both have potential ability in application to technological operations and fatigue or corrosion life control. The non-destructive diffraction methods refer to surface layer thicknesses of a fraction to several tenths μm. They can be used to characterize the bulk of the material in destructive mode by removing measured layers. Application of synchrotron X-ray source enables investigation across bulk of material in nondestructive mode. Particular features of diffraction patterns like angle position, shape and intensity are used to characterize phase composition, residual micro- and macrostresses, crystallographic texture, lattice parameter, defect density and crystalline size. In this case four samples were examined in goal to have nondestructive methodology to characterize some chosen quality parameters of products made of diffusion-alloyed DistaloyAE and DistaloyHP. SAMPLE DESCRIPTION The samples were in a form of ISO3928 fatigue test bars with a thickness of 5 mm. The four sintered materials included in the investigation are described in Table 1. Molybdenum is added by diffusion alloying to DistaloyAE and by pre-alloying the basepowder in DistaloHP. For testing of proposed and elaborated methods one point on samples was chosen (Fig. 1). Table 1. The investigated samples as sintered, alloying elements and carbon addition Tabela 1. Skład chemiczny spiekanych próbek ID Base powder Cu Ni Mo C-UF4 graphite, % A5 0.5 A8 Distaloy AE 1.75 4 0.5* 0.8 H6 0.6 H8 Distaloy HP 2 4 1.5** 0.8 *: diffusion-alloyed **: pre-alloyed METHODOLOGY AND MEASUREMENT - X-RAY DIFFRACTION ANALYSIS Effective penetration depth (EPD) Surface layers of different [...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 79736 "Structural characterizati..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma