Thermodynamics and microstructure of the Cu-Ni-Sn-Ti-Zn alloys

JOLANTA ROMANOWSKA

nr katalogowy: 79735

Tin and zinc are prospective constituents of multicomponent leadfree solders [1], and cooper and nickel are common substrate materials [2], while alloying with some small quantities of titanium influences the wetting and mechanical properties of some materials [3]. Therefore, systems containing these elements seem to be worth carrying out the thorough examination. Binary and ternary alloys constituting the investigated Cu-Ni-Sn-Ti-Zn system were studied by many authors [3÷7], there are only some thermodynamic [8], and calorimetric and structure studies [9] for the quaternary Cu-Ni-Sn-Zn alloys. No literature date was found concerning the Cu-Ni-Sn-Ti-Zn alloys. This paper presents results of some thermodynamic research into Cu-Ni-Sn-Ti-Zn alloys regarding Zn activity measurements by means of the vapour saturation method. EXPERIMENTAL PROCEDURE AND RESULTS The analysed alloys show considerable differences between the vapour pressures of their elements at T = 1373 K: p* Sn= 0.16 Pa, p* Ni = 3.87·10-4 Pa, p* Cu= 6·10-2 Pa, p* Ti = 1.4·10-5 Pa, p* Zn = 4.9·105 Pa [10]. As the vapour pressure of Zn is much higher than that of the other elements, the activity measurements of Zn were carried out by the comparative method of equilibrium vapour saturation. This method has been successfully applied for multicomponent alloys with one volatile component [8, 11, 12]. The studied Cu-Ni-Sn-Zn mixture and the reference mixture Sn-Zn were placed inside a closed crucible under reduced argon pressure and saturated with the zinc vapour until an equilibrium was reached (Fig. 1). At the equilibrium state, the activity of Zn is the same in all mixtures inside the closed system. If the activ[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 79735 "Thermodynamics and micros..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma