Microstructure and corrosion resistance of Ti oxidized at high potentials

nr katalogowy: 79711

Titanium is a basic metallic material used for hard tissue implant applications. It is used in the pure form as a cp-Ti, in alloys and composites [1÷3]. In medical applications the surface state is very important, because it is in direct contact with human body tissue and liquids. Hence the surface should provide a suitable: - corrosion resistance, - biocompatibility, - porosity, - roughness, - wettability. These properties are provided usually by inert ceramic layer - in the case of Ti - usually TiO2. The properly made surface layer separate metallic core from the hazardous environment, preventing release of the harmful ions/compounds from the corroded metallic implant into the body and from the body into the metallic implant core. The TiO2 can be formed in the electrochemical process of anodic oxidation. In the process, current, providing adequate ions flow into/out of the surface, flows across the sample immersed in electrolyte. So, beside oxidation, the dissolution (etching) proceeds, giving a different surface morphologies. In the anodic oxidation of titanium, the electrolytes usually contains the main acidic component, such as: H3PO4, CH3COOH, or H2SO4 [4, 5]. In the Ti anodic oxidation, the dissolution is enhanced mostly by HF or NH4F addition to the electrolyte [6], providing F-type species. Unfortunately, fluoride ions form soluble [TiF6]2 complexes, which results in dissolution of the titanium oxides. In this way the dissolution process limits the thickness of the porous layer [7]. Application of electrolyte containing phosphorus, for example H3PO4, lead to incorporation of phosphorus into the oxide layer. Because phosphorus is a basic component of the human bone, its increase content in the surface layer can improve the osseointegration. The formed anodic oxide layer is mostly porous or in the form of nanotube [8, 9]. Anodic oxid[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 79711 "Microstructure and corros..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma