Structure of TCP layer deposited on surface of NiTi shape memory alloy

nr katalogowy: 79709

The NiTi shape memory alloys with their chemical composition close to the equiatomic have been widely used in medical applications [1, 2]. However, the long-term applications of these alloys can be limited by a corrosion and release of Ni ions [3, 4]. In order to improve the corrosion resistance and protect a human body against harmful influence of released Ni ions, the surface of the NiTi alloys is covered by different protective coatings with diamond-like phases, titanium oxides, titanium carbides and nitrides, polymers or apatites. Moreover, the use of apatites, as a material for surface coating, improves osteoiductivity [5÷7]. Most of the deposition processes require increase in temperature what can lead to decomposition of the B2 phase to equilibrium ones (Ni3Ti and/or NiTi2). The shape memory effect (SME) is closely correlated to the reversible martensitic transformation occurring between the parent B2 phase and martensite. Decrease in amount of the B2 phase results in decrease in the shape memory effect. Also, the SME may be limited by too thick and/or too stiff coatings. In order to improve properties of the NiTi alloy, the passivation and electrophoretic deposition processes were applied. The papers report results obtained for β-tricalcium phosphate (β-TCP) deposited on the surface of NiTi shape memory alloy. EXPERIMENTAL DATA The commercial NiTi alloy with nominal chemical composition: 50.6 at. % Ni and 49.4 at. % Ti was used as a substrate for β-TCP layers deposition. First, rectangular samples of the alloy were quenched from 850°C to the iced water. Next, they were polished with S[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 79709 "Structure of TCP layer de..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma