Characterisation of microstructure evolution during high temperature creep of CMSX-4 superalloy by TEM, HRSTEM and high spatial resolution EDX mapping

nr katalogowy: 78023

CMSX-4 is a single crystal nickel-base superalloy, applied for aircraft and stationary gas turbine blades. Its microstructure consists on the cuboidal precipitates of ?Á?Ś phase (Ni3Al-based), coherent with ?Á solid solution matrix. Chemical composition of CMSX-4 superalloy contain s more than 10 chemical elements and is especially designed to achieve around 70% volume fraction of ?Á?Ś phase. The ?Á.?Á?Ś interfaces, separating the disordered ?Á solid solution and ordered ?Á?Ś phase precipitates, are the strong obstacles for dislocation movement, what allows to obtain the high temperature strength. During exploitation, the turbine blades are subjected to the load by centrifugal force at high temperature in the range from 700 to 1100?‹C, thus undergo creep deformation. The parts of the turbine blade work at different temperatures and stresses, therefore microstructural changes caused by creep must be investigated over a wide temperature.stress range. Depending on the temperature and stress, three creep regimes with distinct modes of predominant microstructural changes in single crystal superalloys can be distunguished [1]: .. at intermediate temperature (700?€850?‹C) and high stress (550?€900 MPa) a pronounced primary creep deformation up to even 5% occurs at the very short time of several hours, .. at high temperature (850?€950?‹C) and medium stress (150?€550 MPa) the tertiary creep is dominant with the creep strain increasing monotonically with creep strain, .. at high temperature (900?€1200?‹C) and low stress (50?€185 MPa) the creep curves display small creep-hardening and a distinct plateau, during which the creep strain is almost not varied with time, followed by the pronounced increase of creep strain leading rupture. The microstructural changes caused by creep of CMSX-4 superalloy at the above mentioned creep regimes have been investigated by many researchers, e.[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 78023 "Characterisation of micro..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2013-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2013-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma