Influence of low-temperature oxynitriding glow-discharge treatment on corrosion resistance of NiTi shape memory alloys

nr katalogowy: 76444

NiTi shape memory alloys are used for cardiac and bone implants. However, due to metalosis, i.e. the migration of the alloy constituents into the surrounding tissues, they undergo various surface treatment processes in order to improve their corrosion resistance. In this article, a comparative study of NiTi alloys’ corrosion resistance both prior and after oxynitriding glowdischarge treatment in a low-temperature plasma process at the temperature of 300 °C is presented. Examinations with the use of potentiodynamic and impedance spectroscopy methods were carried out, which show a corrosion resistance increase of NiTi shape memory alloys after glow-discharge assisted oxynitriding. Corrosion resistance tests were supplemented by morphology and roughness tests carried out on NiTi alloy surfaces both with and without a diffusive layer. Keywords: shape memory alloys, oxynitriding, low-temperature process, corrosion resistance.Introduction Shape memory alloys are being more and more widely used in medicine, as medical bone or cardiac implants used to, e.g. connect bones, adjust the spine, in orthodontics, or in minimally invasive surgery to seal interventricular septums or in self-expanding stents for endovascular treatment [1]. However, due to the presence of nickel and the migration of alloy components to the surrounding tissues (metalosis), their use in implantology, especially in long-term implants, requires their corrosion resistance to be improved. This is accomplished through the use of various methods of surface treatment, which lead to the formation of titanium oxide or carbon layers on the metal surface, such as DLC (diamond like carbon), pyrolytic carbon, NCD (nanocrystalline diamond), titanium nitride, or polymer [2] and ceramic coatings. The following surface treatment processes are being studied: electrochemical oxidation, RFCVD, MWCVD, ion implantation, zol-gel method, glowdischarge nitriding [4-8]. A lim[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 76444 "Influence of low-temperat..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-5 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma