The effect of reactive elements on high temperature oxidation of FeCrAl alloy

nr katalogowy: 76442

One-layer protective coatings made up CeO2 oxides were synthesized on a Fe- CrAl alloy substrate by the sol-gel method from sol containing cerium(III) 2,4-pentanedionate as the precursor. It was found that a small addition of cerium affected the morphology of the forming coatings and improved the Fe- CrAl alloy resistance to high-temperature oxidation (in air at T = 950°C for t = 100 h). The oxidation of all the investigated samples conformed to the parabolic rate. The protection effectiveness of the one-layer coatings after 100 h of high-temperature oxidation was as high as 70%. Keywords: ceramic, CeO2 coatings, high temperature corrosion, sol-gel, FeCrAl.1. Introduction Metallic materials which are operated at high temperature should exhibit a suffi cient heat and creep resistance. Protective properties of many alloys are connected with formation of the accumulating scale, usually of an aluminum oxide [1]. Alloys of the FeCrAl type are the material which is often used to be operated at a temperature close to 1400°C. In practice, the alloys are being used at a lower temperature, below 1000°C, for instance as carriers of catalytic converters for gasoline run vehicles [2]. High temperature tolerance of the FeCrAl alloys depends on the properties of the increasing scale of aluminum oxide (Al2O3) [3]. The growth an accumulation processes of the scale during oxidation in the temperature range from 800 to 1000°C are complicated. This results from the presence of transient aluminum oxides (γ-, δ-, θ-) which transform into a stable phase of α-Al2O3. Desirable protective properties of the α-Al2O3 type of scale are due to, among others, a low accumulation rate [1], a low concentration of crystal faults [4] and a good chemical stability at high temperature [5]. During cyclic oxidation, however, the scale may undergo cracking and spalling [6, 7]. Adding reactive elements (RE) such as Zr, Hf, Y, Ce, La [8[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 76442 "The effect of reactive el..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-5 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma