Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2013 - zeszyt 5

The infl uence of cutting steel S355JR on the nature and corrosion resistance of the zinc coating

nr katalogowy: 76440

Paper presents the results of investigation regarding the infl uence of the surface state of steel S355JR achieved after different cutting methods on the structure and corrosion resistance of the zinc coating. Research was focused on fi ttings for overhead power lines - a double eyes links type SLINK. In the process of samples cutting the following methods were used: waterjet, laser and fl ame cutting. Prepared materials were subjected to an abrasive blasting - steel shot GL40 and chemical treatment - pickling (hydrochloric acid) and fl uxing (TIBFLUX60). The hot - dip Zn galvanizing process was conducted in industrial conditions. Parameters were fi xed (temperature 460oC, dipping time 2,5 min). The effects were evaluated on the basis of metallographic analysis and corrosion tests (according to PN-EN ISO 9227). It was found out that the hot-dip zinc coating on the water-jet cutting surface demonstrates the best corrosion resistance. The corrosion resistance of the zinc coating on laser cutting surface is better than on fl ame cutting surface. The fl ame cutting surface needs additional mechanical (grinding) or electrochemical (electropolishing) processing. Keywords: laser cutting, water cutting, oxygen cutting, heat affected zone, abrasive blasting, chemical treatment, zinc coating, hot-dip zinc galvanizing, corrosion resistance.1. Introduction The industry use in the wide range the mechanical forming: fl ame cutting (oxygen plasma), laser, water JET or water-abrasive cutting and electrical discharge. Cutting methods differs in the amount of consumed energy, the impact of heat on the material and the quality of the cutting edge. The comparison of cutting method is shown in Table 1[1, 2]. The applied method infl uence among others on the structure and properties of outer layer - that depend on the creation of so-called Heat Affected Zone (HAZ). The HAZ thickness depends above all on process temperature and beam concentration[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 76440 "The infl uence of cutting..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-5 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma