The evaluation of zinc coatings corrosion resistance on the ambulance construction elements

nr katalogowy: 75764

The mobile character of the ambulance functioning, as well as applying strong disinfectants support the phenomenon of the corrosion and the adhesion of micro-organisms on the abiotic surfaces. Zinc-plated coatings demonstrate properties suppressing bacterium growing. The presented paper describes research fi ndings of the corrosion resistance of construction elements of the sanitary ambulance protected by zinc-plated coatings. Research was focused on the steel grade D01, which is widely used as the construction material of the medical equipment. After mechanical treatment (grinding and polishing) samples were divided into three groups that were subjected to the zinc coating. The following methods of zinc coating were applied: galvanic (two applications according to EN ISO 4042), hot-dip (PN-EN ISO 10684) and lamellar (PN-EN ISO 10683). The scope of research included roughness and surface topography measurements as well as metallographic observation and corrosion tests. Conclusions were formulated basing upon the tests made in the salt chamber - NaCl (acc. PN-EN ISO 9227). It is clear that the zinc coating with new passivation thick layer protects the steel base material in the best way. There was no white corrosion on the lamellar zinc surface. Keywords: white corrosion, salt chamber, hot-dip zinc galvanizing, zinc plating, lamellar zinc.1. Introduction Steel parts used in medical institutions are protected against the corrosion by metallic and paint coatings. The most frequently the following coatings are applied: Ni, Cr, Cu, as well as hot dip or galvanic zinc. Hot dip zinc coating is less applied due to the high value of roughness and aesthetics. Protection of the medical equipment against the corrosion is a substantial problem. The attack of chemical agents and the bacterial fl ora reduce the corrosion resistance of coatings. The appearance of the local corrosion results in growing of the bacte[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 75764 "The evaluation of zinc co..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma