Corrosion studies of amorphous and crystalline Mg36,6Cu36,2Ca27,2 alloy in physiological fl uid

nr katalogowy: 75759

The aim of this paper is to investigate the electrochemical corrosion resistance of metallic glass Mg36,6Cu36,2Ca27,2 in as-cast state and after annealing. In the work was carried out studies of the structure of the analyzed samples using X-ray diffraction and microscopic observation. In order to determine the dissolution rate of the tested alloy Mg36,6Cu36,2Ca27,2 and potential suitability for biomedical applications were carried out immersion test and potentiodynamic test electrochemical corrosion in a physiological fl uid (electrolyte solution). It was found that Mg36,6Cu36,2Ca27,2 alloy with amorphous structure has a much higher corrosion resistance than the same alloy with crystalline structure. Keywords: potentiodynamic tests, immersion tests, corrosion resistance, amorphous structure, magnesium based alloys.1. Introduction In recent years, magnesium based alloys have been attractive because of the possibility of using them as potential materials for orthopedic implants. In comparison to the commonly used metallic orthopedic implants, such as titanium alloys, cobalt chromium and stainless steel, magnesium alloys are characterized by a lower Young’s modulus (40÷45 GPa), and density (1.7÷2.0 g/ cm3), which are similar to the properties of human bone. Interest in magnesium alloys is not only motivated by their good mechanical properties, but also the possibility of biodegradable implants in the human body, which would exclude the need for re-operation [1, 2]. The main research problem related with the concept of alloys for biodegradable medical implants is to ensure proper (guaranteeing the bone adhesion) time to move required stress by implant, associated with respectively matched dissolution time of the implant in the body fl uids. Both the strength and dissolution rate in body fl uids under certain conditions depending on the structure and the chemical composition of the implant. Therefore, it should be sea[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 75759 "Corrosion studies of amor..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-4 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma