Hot corrosion resistance of γ-TiAl alloy during oxidation in hydrochloric atmosphere

JOANNA MAŁECKA

nr katalogowy: 74464

Test results of isothermal oxidation of γ-TiAl-based Ti-46Al-7Nb-0,7Cr- 0,1Si-0,2Ni alloy in an atmosphere of 9% O2 + 0,2% HCl + 0,08% SO2 + N2 are presented. Oxidation was carried out at 700º. It was found that Ti-46Al- 7Nb alloys show good high-temperature corrosion resistance. Keywords: high temperature corrosion, γ-TiAl, oxidation.1. Introduction Alloys, whose microstructures are made up of organized Ti-Al-system intermetallic phases, have signifi cant potential in fi nding use in high-temperature applications [1-3]. Their low density, relatively high melting temperature, good mechanical properties at high temperatures, hardness, resistance to creep, resistance to stress and fatigue cracking make them useful in industrial applications. They are a new generation of construction materials which fi nd application in the production of valves for combustion engines, gas turbine blades, turbo charger rotors or even supersonic structures [4]. These alloys, thanks to their properties, are used to operate at temperatures exceeding 600°C, where classic titanium alloys fail due to their low resistance to oxidation. To increase the scope of application and reliability of this group of materials, many scientists have recently been conducting research involving the manufacture of a surface layer or a protective coating on the surface of the said alloys. The research so far conducted by the author of this paper has proven that application of an Al2O3 [5] coating improves resistance to high temperature oxidation of a γ-TiAl alloy in an atmosphere of air, which is very promising. As a result, combining a protective coating with a suitable microstructure should make the materials usable at temperatures of up to 950°C [6]. However, not only temperature impacts the course of the oxidation process. The intensity of high temperature corrosion processes clearly depends on the atmosphere of the oxidising environmen[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 74464 "Hot corrosion resistance ..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2013-2 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2013-2

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma