Pattern selection within the stripes strengthening the hexagonal (Zn)-single crystal

nr katalogowy: 71586

A phenomenon of strengthening is observed for the hexagonal (Zn)-single crystal equipped with regular stripes which contain the Zn16Ti intermetallic compound. It is well known that the strengthening by the addition of some particles or elements is available [1, 2]. Usually, the strengthening leads to significant increasing of some mechanical properties of a given single crystal. The studied hexagonal (Zn)-single crystal was doped by the small amount of titanium and copper. The addition of copper modifies the specific surface free energy at the solid/liquid interface. Copper does not form an intermetallic compound with the zinc but is localized in the zinc/titanium solid solution, (Zn). However, titanium forms an intermetallic compound with the zinc, Zn16Ti. The (Zn)-Zn16Ti system is the pseudobinary eutectic system. It gives an opportunity to control the growth of the Zn hexagonal single crystal, and first of all to control the thickness of the stripes which appear cyclically within the single crystal (Fig. 1). Moreover, the imposed changes of the growth rate select the pattern within stripes strengthening the (Zn)-single crystal. Therefore, two threshold growth rate were recorded: v1 - at which L-shape rod like structure (irregular eutectic structure) transforms into lamellar structure (regular eutectic structure), v2 - at which lamellar structure transforms into rod-like structure (regular eutectic structure). Some transformations from rod-like into lamellar structure are known, especially in the Al-Si and Fe-C eutectic systems [3÷9]. Analogously to the Al-Si and Fe-C eutectic the Zn-Zn16Ti eutectic also evinces irregular structure but[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 71586 "Pattern selection within ..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2012-5 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2012-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma