Modelling of melt-spinning process of amorphous tapes using the artificial neural networks (ANN)

nr katalogowy: 62461

The first commercial scale production of amorphous materials was started in 1979 by Allien Chemical Corporation. Obtained amorphous tapes had a thickness range of 30÷50 μm and width at about ten-odd mm. The another metallic glass tapes are produced in Germany (Vacuumschmelze) and Japan (Hitachi Metals) [1]. The tapes with thickness range of 50÷100 μm and width from 2 to 5 mm are made in Institute of Physics, Czestochowa University of Technology. The melt-spinning method is used for moulding. In order to produce amorphous tapes it is crucial to accurately prepare the alloy for moulding. The substrate elements must to have a high chemical purity. The chemical constitution of molten alloy includes transition metals, for example Fe, Ni, Co or their combinations, and semi-metals, for example B, P, C, Si or their combinations. It’s very important, that the chemical constitution of alloy includes about 70÷80% of semi-metal, for example iron [2]. Selection of proper chemical composition of alloy minimizes possibility of material crystallization. To obtain amorphous materials the following conditions must be satisfied: -- prepared alloy is composed of more than three elements, -- variation in atomic radius of elements in the alloy exceed 12%, correct packing of atoms is allowed, -- the main components of the alloy are characterized by negative heat of mixing, which influences viscosity of the obtained material [3]. Fundamental problem of process is getting of high cooling velocity, in order to glass transition of material. Satisfying all above conditions causes a cooling velocity range of 10-1÷103 K/s. Moreover, that cooling velocity for amorphous tapes produced by using melt-spinning method (one-direction cooling alloy into rotating copper drum) is contained in range from 104 to 106 K/s [3]. Production of amorphous tapes by melt-spinning method depends on chemical constitution of the alloy, and is carried out in ine[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 62461 "Modelling of melt-spinnin..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2011-4 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2011-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma