Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2012 - zeszyt 5

Nanocrystallinie TiNi, Ti2Ni alloys for hydrogen storage

nr katalogowy: 71591

In the last decade a great interest has been observed in the field of nanoscale materials. Mechanical alloying (MA) has been proved to be a novel and promising method for alloy formation, especially in the preparation of non-equilibrium materials of various systems [1÷7]. This technique has already succeeded in obtaining a wide range of alloy hydrides for energy storage or other energy related applications [2, 4÷11]. The advanced nanocrystalline intermetallics are representing a new generation of metal hydride materials with the following characteristics: high storage capacity, stable temperature- pressure cycling capacity during the life-time of the system, good corrosion stability and low costs. These materials exhibit quite different properties from both crystalline and amorphous materials, due to structure in which extremely fine grains are separated by what some investigators have characterized as "glass-like" disordered grain boundaries [3, 4]. Therefore, the hydrogenation behaviour of the amorphous structure is different than that of the crystalline material. Mechanical alloying has recently been used to make an amorphous and nanocrystalline TiFe, ZrV2-, LaNi5- and Mg2A-type alloys (A = Fe, Co, Ni, Cu) [6÷11]. These materials show substantially enhanced absorption and desorption kinetics, even at relatively low temperature [9, 10]. Among the different types of hydrogen forming compounds, Ti-based alloys are among the promising materials for hydrogen energy applications [6, 7, 12, 13]. For example, the TiNi alloy, which crystallizes in the cubic CsCl-type structure is lighter and cheaper than the LaNi5-type alloy. Nevertheless, the application of TiNi material in batteries has been limited due to poor absorption/ desorption kinetics in addition to a complicated activation procedure. To improve the activation of this alloy several approaches have been adopted. For example, ball milling of TiNi is effective for the improve[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 59362 "Systemy szybkiego diagnoz..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2012-5 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

WIADOMOŚCI ELEKTROTECHNICZNE - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

WIADOMOŚCI ELEKTROTECHNICZNE - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
WIADOMOŚCI ELEKTROTECHNICZNE - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
WIADOMOŚCI ELEKTROTECHNICZNE - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

534.00 zł

WIADOMOŚCI ELEKTROTECHNICZNE - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
WIADOMOŚCI ELEKTROTECHNICZNE - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2012-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma