Texturization of polycrystalline silicon by metal assisted chemical etching

Marek Lipiński

nr katalogowy: 52794

Cell reflectance is one of the factors influencing the efficiency of silicon solar cells. Therefore, the reduction of optical losses can significantly improve the efficiency of the solar cell. At present, the monocrystalline silicon wafers with (100) crystallographic orientation are textured by an anisotropic alkaline chemical etching. However, this method is not suitable for polycrystalline silicon due to different crystallographic orientations of the crystal grains. On the other hand, an isotropic acidic texturization based on a HF/HNO3 etching solution gives better results for polycrystalline silicon because every grain orientation is etched with the same rate. Unfortunately, isotextured mc-Si solar cells still suffer from high surface reflection. The new method of texturization is based on metal-assisted chemical etching (MAE). It was shown that MAE can produce the black silicon with very low surface reflectivity [1]. It is based on the deposition of metal clusters (Au, Ag, Pt, Pd) as catalyst for chemical etching in a solution containing HF acid and an oxidizing agent [1÷8]. In this work, palladium is deposited as a catalytic metal by immersing silicon wafers in PdCl2 aqueous solution [9÷12]. A metal assisted etching in HF:H2O2:H2O forms a porous Si. The consecutive chemical etching based on HF:HNO3 solution change the porous structure into the textured surface, which is more convenient for solar cells than the porous layer. EXPERIMENT AL AND RESU LTS Palladium clusters deposition The p type polycrystalline silicon wafers with resistivity ρ of 0.5 to 2 &#[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52794 "Texturization of polycrys..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma