Quantitative evaluation of γʹ phase in CMSX-4 superalloy

nr katalogowy: 52770

The microstructure of nickel-base superalloys determines their mechanical behaviour. The strength of Ni-base superalloys is dependent on such factors as volume fraction, size, coarsening rate, and composition of γʹ phase precipitates [1]. The content and size of γʹ phase precipitates embedded in a cubic face-centred γ matrix can be adjusted by the alloy design and heat treatments. The composition of the ordered γʹ precipitates does differ, i.e. Ni3(Al, Ti, ...), and depends on the alloy composition and processing [2]. The characterization of γʹ phase precipitates in different nickelbased superalloys has been the subject of extensive research work. Volume fraction of the γʹ phase in Ni-base superalloys is a significant element influencing on working out the superalloys chemical compositions [3]. MATERIAL The measurements of γʹ phase precipitations were carried out on a monocrystalline cylindrical bar of 8 mm diameter made of CMSX-4 nickel-base superalloy [4]. The bar was cast in Laboratory of Material Research for Aircraft Industry in Rzeszów. The material was investigated in the as-cast condition. IMAGE ACQUISITION AND ANALYSIS OF γʹ PHASE PRECIPITATES The bar intended for investigations was cut perpendicularly to the main axis. The procedure of metallographic specimen preparation was described in details in Table 1. Quantitative metallography of CMSX-4 requires the revealing of γʹ precipitates by means of an appropriate etching conditions selection as well as use of appropriate image acquisition in order to observe the γʹ precipitates and register the images of the superalloy microstructure with them. In the previous work two etching methods of the γʹ phase precipitates were described [5]. For a quantitative evaluation of the precipitates etchant caused their etching and leaving the γ matrix is better, so in the ca[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52770 "Quantitative evaluation o..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma