TEM analysis of creep mechanisms of single-crystalline nickel-base superalloys

nr katalogowy: 52751

Single crystal (SC) superalloys are especially designed for gas turbine blades in jet aircraft engines and stationary turbines generating electricity. The basis criterion in material selection for gas turbine blades is a high creep strength, because they have to withstand centrifugal forces acting during operation. The main creep mechanisms in polycrystalline superalloys are: -- dislocation creep by combined slip and climb of dislocations, -- diffusion creep by Nabarro-Herring or Coble mechanism [1, 2]. As it was shown for many superalloys [3÷5], in the range of temperature and stresses characteristic for service conditions of turbine blades, grain boundary diffusion by Coble mechanism is the main factor controlling the creep rate. Therefore the elimination of grain boundaries is necessary for improvement of creep resistance of superalloys. It can be achieved by a directional solidification with a grain selector, as was demonstrated first by B. Piearcey from Pratt & Whitney in 1970 [6]. Single crystal superalloys exhibit the highest creep resistance among metallic materials. The development of chemical composition of SC superalloys resulted in elaboration of four generations of these alloys [7, 8] and progress continues already towards the fifths generation [9]. The as-cast single crystal superalloys exhibit a dendritic structure with the eutectic areas between dendrite arms, which can be homogenized by heat treatment. The typical microstructure consists of about 70% of cuboid γʹ precipitates, about 400 nm in size, separated by γ matrix channels about 30 nm wide. Residual eutectic areas contain large irregular γʹ precipitates. Such two-phase microstructure guarantees the high creep resistance of single-crystalline turbine blades. The γʹ precipitates are an ordered Ni3Al-base intermetallic phase with the lattice parameter only slightly smaller than the Ni-base γ solid solution. This produc[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52751 "TEM analysis of creep mec..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma