Ball milling amorphization and consolidation of NiTiZrNb and NiNbTiZrCoCu alloys

nr katalogowy: 52722

Amorphous nickel rich alloys have been obtained in recent years by rapid quenching from the liquid state or by mechanical alloying in a planetary mill [1÷9]. One advantage of the latter method is that it makes it possible to obtain new materials from powders of different elements, which are immiscible in the liquid state. Binary NiTi alloys subjected to ball milling or severe plastic deformation can be obtained amorphous [1÷3]. The tendency to form an amorphous structure depends on the relative values of the deformation temperature and martensite start (Ms) temperature. Lowering of the deformation temperature in the range below the martensite finish temperature facilitates amorphization [3]. Mechanical alloying of Ni60Nb20Zr20 alloy [4] involves two consecutive amorphization reactions, leading first to the amorphization reaction between Ni and Zr layers and on further milling consequently a Ni-Nb amorphous phase forms. The resulting two amorphous phases homogenize at longer milling times. Multicomponent nickel base alloys can be obtained as bulk glass at composition of Ni50Co10Nb20Ti10Zr10 (at. %) alloys with reported large supercooled liquid region of more than 40 K formed by copper-mold casting. The alloys with 5 and 10 at. % cobalt possess the highest glass-forming ability [5]. Mechanically alloyed Ni57Zr20Ti18Al5 alloy powders synthesized by high-energy ball milling have shown a complete amorphization after 5 h of milling, even broader supercooled region of 56°C and crystallization temperature above 500°C [6]. Substitution of aluminum by silicon [7] also allowed to obtain amorphous Ni57Zr20Ti20Si3 powders by mechanical alloying of pure Ni, Zr, Ti, Si, and ceramic powder mixture; the metallic alloy amorphized after 5 hours milling indicating a good glass forming ability. In [8] Amorphous Ni59Zr20Ti16Sn5 alloys were fabricated by melt spinning and by mechanical alloying (MA) techniques. Differences in crystallization temperat[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52722 "Ball milling amorphizatio..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma