MgH2 and intermetallic hydride nanocomposites synthesized by mechanical ball milling

nr katalogowy: 52711

One of the obstacles to the implementation of the Hydrogen Economy into automotive industry is a lack of viable hydrogen storage system. Relatively promising is hydrogen storage system based on solid state hydrides with high hydrogen capacities exceeding 6 wt. %. However, a number of high capacity hydrides have high desorption temperatures which are incompatible with the waste heat generated by an automotive PEM (Proton Exchange Membrane) fuel cell. The search for materials that match the DOE criteria for hydrogen storage materials to be used in automobile applications has been largely focused on hydride composites in the past ten years [1÷5]. Very recently, it has been shown [4, 5] that the hydrogen desorption temperature of the composite constituent with the higher desorption temperature in the systems, substantially decreases linearly with increasing volume fraction of the constituent having lower desorption temperature. In the present work the composite approach is applied to the MgH2 + FeTi and MgH2 + LaNi5 systems. The composites with various volume fractions of both constituents were processed by controlled reactive milling (CRM) in a magneto-mill (under hydrogen atmosphere). Hydrogen desorption was tested using a Differential Scanning Calorimeter (DSC) and Temperature Programmed Desorption (TPD) analysis. The aim of this work is to analyze the influence of intermetallic additives on magnesium hydrogen decomposition process in MgH2 + FeTi and MgH2 + LaNi5 composites. experimental As-received commercial MgH2 powder (Sigma-Aldrich; ~98 wt. % purity; the remaining Mg), LaNi5 (Alfa Aesar, hydrogen storage grade) and cast FeTi intermetallic powder, were mixed to MgH2 + X wt. % FeTi and MgH2 + X wt. % LaNi5 (where X = 10, 30 and 50) compositions. As a reference MgH2 without additives was used. The FeTi intermetallic powder was obtained by melting pre-compressed Fe and Ti powders mixture and grinding the obtained ingot. Gr[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52711 "MgH2 and intermetallic hy..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma