Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2010 - zeszyt 3

Capabilities of Al2O3 nanolayer formation on carbon fibers by CVD method

nr katalogowy: 52696

Carbon fibers are characterized as materials with low oxidation resistance in an oxidative environment and chemical reactivity limits their application in metal-matrix composites. To widen the application of carbon fibers in a metal composite some form of coating is needed which may improve their oxidation resistance at high temperatures and to give the possibility of the fiber/matrix interfacial reaction control [1÷4]. In fact, several techniques such as chemical vapor deposition (CVD), physical vapor deposition (PVD), the solgel method and other modern techniques can be used to provide coating for carbon fibers. Alumina coating in comparison with other coatings seems to be very attractive, simply because of the low precursor material price. The most frequent technique used to obtain oxide coatings like alumina, silica, zirconia and titania is the sol-gel method. In the case of an organometallic solution application, fibers are passed through a solution and the coating is formed by hydrolysis of the organometallic compounds. The oxide coating homogeneity and thickness can be controlled by the appropriate selection of the solution concentration, immersion time and temperature [1, 3÷7]. Alumina coatings obtained on the carbon fibers by sol-gel method only partially prevent the oxidation of carbon because of the presence of pores [3]. However some authors [6] report that the porous alumina coatings obtained on fibers by sol-gel act not only as diffusion barriers (improving the oxidation resistance of carbon fiber and preventing harmful CF/Al interfacial reactions), but also promote wettability and relieve thermal stress concentration between the carbon fibers and the aluminum matrix. The other technique used to obtain thin al[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52696 "Capabilities of Al2O3 nan..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma