Microstructure of the surface layer of a Ti6Al4V alloy and X5CrNi18-10 steel after laser treatment

nr katalogowy: 52681

One of the relatively new method of mechanical surface treatments is Laser Shock Processing (LSP), which introduce strain hardening and compressive residual stresses into the treated surface layer. LSP uses laser pulses with pulse duration within the nanosecond range to modify the surface layers by means of high pressure [1, 2]. Laser parameters for LSP require power density ≥0.1 GW/cm2 and laser pulse duration ≤10-6 s. During the process, the laser beam is directed onto the surface of the material. The area to be treated is usually covered with two types of coatings: an absorbing coating, opaque to the laser beam, for example black paint, placed directly on the surface of the investigated material, and over this a transparent to the laser beam coating for example water [3, 4]. Figure 1 shows the scheme of the Laser Shock Processing. When the laser beam with sufficient intensity is directed onto the surface, it passes through the transparent layer and is absorbed by the black coating. The absorbing coating is vaporized and the vapor rapidly achieves very high temperatures at which electrons are ionized and a plasma plume is formed. The rapidly expanding plasma is confined on the surface of the metal by the layer of water, creating high pressures. This pressure propagating into the treated material as a shock wave, can induce microstructural changes and cause high increase of dislocation density and produce a high residual surface compressive stresses [5, 6]. The aim of this work was to investigate the effect of Laser Shock Processing on the microstructure and roughness of the surface layer of the Ti6Al4V titanium alloy and X5CrNi18-10 austenitic stainless steel. MATERIALS AND E[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52681 "Microstructure of the sur..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma