Characterization of titanium nitride layer on titanium alloy

nr katalogowy: 52679

Titanium and titanium alloys are widely used at some technical and medical applications because of their mechanical and corrosion resistance properties. The Ti6Al4V alloy is the most popular and universal alloy, for example it find a use for the aircraft parts and for implants in dentistry and orthopedics [1÷3]. This alloy is produce as cast and as forging. It belongs to the high strength materials but its wear resistance is low. Therefore various methods of surface modification are used [4÷7], e.g. plasma electrolytic oxidation (PEO), electrophoretic deposition (EPD), vacuum plasma spraying, glow discharge, plasma treatment, chemical vapor deposition (CVD). Nitriding of titanium and titanium alloys has been investigated for many years and is used effectively for protection against wear. In this paper the TiN+Ti2N+αTi(N) layer deposited by glow-discharge nitriding on the Ti6Al4V alloy is characterized. This hybrid system is destined as outer layer or intermediate layer under other ceramic in biomedical applications and as thin film for adhesive bonding to polymer composites in aircraft applications. Materials and methods The TiN/Ti2N/αTi(N) layer was deposited on the Ti6Al4V alloy (ASTM grade 5). This hybrid layer was produced by glow-discharge assisted by nitriding in pure nitrogen atmosphere at 1073 K (800°C) and 4 hPa pressure for 3 h. The process was carried out with the use of universal apparatus for different types of thermochemical treatment under glow discharge conditions at Warsaw University of Technology [7, 8]. The thickness of coating was about 40 μm. The phase composition of surface layer was performed by X-ray diffraction technique (XRD). Microstructure and morphology of thin film were analyzed by scanning electron microscope (SEM) with energy dispersive X-ray spectroscopy (ED[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52679 "Characterization of titan..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma