Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2010 - zeszyt 3

Characteristics of surface layers produced on austenitic-ferritic stainless steel by low temperature glow discharge nitriding

nr katalogowy: 52675

Austenitic-ferritic stainless steels are characterized by high strength, better than those of standard austenitic stainless steels, good ductility, high resistance to stress corrosion, low thermal expansion and good weldability. Moreover, thanks to the presence of austenite which is resistant to hydrogen corrosion [1], the resistance to the hydrogen-induced damage of austenitic-ferritic steels is better that that of single-phase ferritic steels. It has been shown, that duplex steels are however romoted to the hydrogen embrittlement [2]. Numerous advantages of these steels make them attractive for many potential applications, e.g. in the food, chemical, petrochemical and paper industries where they can be used for the manufacture of components intended for exploitation in aggressive environments, such as boilers, pressure vessels, installations in the food industry and mining, pipelines transporting natural gas or oil in contact with seawater. These conditions may favour the penetration of hydrogen into the steel, and thereby promote hydrogen corrosion. A method of reducing hydrogen penetration into steel is to produce a nitrided layer on the surface [3, 4]. A phase with especially advantageous properties in this respect is the S-phase (known as expanded austenite γN [5]), which can increase the resistance to frictional wear and significantly reduce the penetration of hydrogen [3, 6], without altering the high corrosion resistance of the steel. The presence of the S-phase formed during the low-temperature nitriding is manifested in the diffraction spectra as a shift of the diffraction peaks, (which accompan[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52675 "Characteristics of surfac..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma