Composition - property relations in low-neodymium Nd-Fe-B-Ti melt-spun alloys

nr katalogowy: 52670

Modification of the properties of Nd-Fe-B magnets by minor addition of other elements has been studied since their development in 1984 [1÷4]. For neodymium contents lower than that for the stechiometric Nd2Fe14B phase, beside the hard magnetic phase, the soft magnetic phases such as α-Fe, Fe3B and Fe2B is present. Such alloys are called magnetic nanocomposites [5÷6]. However, deacrease of the Nd content leads to substantial drop of the coercivity. Thus, we tried to modify of the microstructure of the alloys by addition of small proportion of Ti. In this work the effect of titanium addition was studied for the alloys content of 7, 8 and 9% at. of neodymium. EXPERIMENTAL The initial ingots were prepared by arc melting of pure elements. The Nd7Fe79-xB14Tix, Nd8Fe78-xB14Tix and Nd8Fe77-xB14Tix ribbon alloys (x = 0, 2, 4 at. %) were prepared by rapid solidification of molten alloys by melt-spinning with the roll speed of 20 m/s. The overquenched ribbons were annealed at 953÷973 K for 20 minutes. The microstructure of the annealed ribbons was studied using a JEOL JEM 3010 transmission electron microscope. The phase constitution was evaluated using X-ray diffraction (XRD) (Philips PW 1140, Co). The magnetic properties were measured using a Lake- Shore 7410 vibrating sample magnetometer in maximum external field of 3 T. RESULTS AND DISCUSSION Addition of Ti for the Nd-Fe-B alloys generally resulted in increase of the onset of crystall[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52670 "Composition - property re..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma