Effect of annealing on the structure and properties of Ni46.4Mn28.5Ga25.1 single crystal

nr katalogowy: 52665

Ferromagnetic Heusler alloys are based on the X2YZ phase. The first notice on such alloys comes from Friedrich Heusler et al. who characterized the Cu2MnAl alloy in 1903 [1]. That alloy showed ferromagnetic properties although none of the components was ferromagnetic. In 1934 Bradley and Rodgers reported on the effect of heat treatment of Cu2MnAl alloy [2]. Main conclusion coming from this work is that the ferromagnetism of the Heusler-based alloys depends not only on the chemical composition but also on the positions of neighbouring atoms. The Ni2MnGa-type alloys due to their magnetic field induced strain (MFIS), up to 10%, attract attention of the scientists and engineers. Over ten years of studies, since the first report, the magnetic shape memory effect (MSME) [3] has brought many publications on the structure and properties of the Ni2MnGa alloys. Especially structure of the martensite, its type and forming conditions is an object of great interest of many researchers. Various heat treatment procedures were proposed. For example Gaitzsch et al. have found that annealing at 803 K for 24 h leads in the Ni50Mn30Ga20 alloy to formation of the 7M martensite [4]. In our previous work we studied the effect of annealing temperature and the cooling rate on the structure of the polycrystalline Ni50Mn29Ga21 alloy [5]. It was found that the final structure strongly depends on the conditions of heat treatment and the 7M martensite can be produced by annealing [...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52665 "Effect of annealing on th..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma