Structure of sintered Ni-Ti-Fe shape memory alloys

nr katalogowy: 52663

Properties of NiTi shape memory alloy (SMA) are sensitive to any modification that can change the atom environment. It is due to the occurrence of the reversible thermoelastic martensitic transformation. This transformation is so called “civil" transition and proceeds by a correlated atom shuffle. Among the known modifications of NiTi properties there are changes in the chemical composition [1], thermomechanical treatment [2] and/or manufacturing technique [3]. First of all, the NiTi alloys are sensitive to changes in chemical composition. The raise of titanium contents of 0.1 at. % increases the transformation temperatures of 10 degrees. Moreover, substitution of either nickel or titanium by third alloying element strongly influences thermal behavior. The third element can be use for controlling transformation temperatures, thermal hysteresis width, change of the transformation course and sequences as well as for increase the stability of the transformation temperatures [4]. For example addition of zirconium or hafnium increases transformation temperatures [5], whereas cobalt, iron or aluminum decreases of their values [6]. Copper reduces [7] while hafnium [5] broadens thermal hysteresis of the martensitic transformation. In comparison to a binary NiTi alloy, addition of iron or cobalt causes change in the course of the martensitic transformation. In the NiTi alloy the B2 parent phase transforms directly to the B19´ monoclinic martensite. In ternary NiTiFe or NiTiCo alloy this transformation is preceded by additional phase transition - the R-phase transformation [8]. It is worth to note that the B2-R-B19´ transformation sequence can occur without any special thermal or thermo- -mechanical treatment. In order to directly influence the martensitic transformation the nonconventional production techniques such as powder metallurgy (PM) [9], melt-spinning (MS) [9] or twin roll casting (TRC) [10] for manufacturing the NiTi-ba[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52663 "Structure of sintered Ni-..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma