Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2010 - zeszyt 3

The effect of lattice distortion on the course of the martensitic transformations in NiTi shape memory alloys

nr katalogowy: 52662

In the Ni-Ti system it is the B2 intermetalic NiTi phase that undergoes the reversible martensitic transformation to the B19′ monoclinic phase. For an alloy of any composition (provided it ensures the B2 phase presence) cooled down very slowly the transformation occurs always at the same temperature i.e. about 60°C. In the Ni-rich alloys the precipitation process may take place that changes the transformation characteristic temperatures and/or its sequence. There are several variants of this process depending on the ageing temperature [1], these are: β0 → β1 + Ni4Ti3 → β2 + Ti2Ni3 → β3 + TiNi3, Ta < 680 ± 10°C β0 → β′1 + Ni3Ti2 → β′2 + TiNi3, 680 ± 10°C < Ta < 750 ± 10°C β0 → β″1 + Ni3Ti for Ta > 750 ± 10°C. However, the most significant influence on the course of the martensitic transformation in the NiTi alloy have the Ni4Ti3 particles. The strain fields around these coherent precipitates as well as the decrease of the Ni concentration in the matrix change the characteristic transformation temperatures and cause occurrence of the R-phase transition preceding the B19′ martensite formation. Similar effects take place in the NiTi equiatomic alloys deformed and then annealed at temperatures below the recrystallisation temperature. In both cases additional effects in form of a multistage transformation were often observed. The first data on the multistage martensitic transformation were given by Todoroki and Tamura [2], Stróż et al. [3] and Zhu et al. [4]. It was found that depending on the applied thermal treatment there exist three or even four more or less overlapping peaks on the DSC cooling curves. The occurrence of the R-phase transition in these alloys is understandable as this transition causes less lattice distortions and thus is favoured when the internal stresses exist in the sample. Howeve[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52662 "The effect of lattice dis..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma