Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2010 - zeszyt 3

Kinetics of phase transformations during tempering of tool steels of a different chromium content

nr katalogowy: 52655

During heating as-quenched martensite, the tempering (of unalloyed, medium and high carbon steels) takes place in three distinct but overlapping stages: precipitation of ε carbide, transformation of the retained austenite into lower bainite and precipitation of cementite. In steels containing alloying elements contributing to an effect of secondary hardening (V, Mo, W) a fourth stage (transformation) occurs: precipitation of MC and M2C-type alloy carbides, that nucleate independently [1÷4]. The first transformation occurs in the temperature range of 100÷200°C. Metastable ε carbide (Fe2.4C) with hexagonal crystal structure precipitates from the supersaturated martensite [5÷8]. Precipitation of highly dispersed ε carbide is believed to enhance strengthening in steel [2, 4]. The second transformation takes place during tempering in the temperature range of 200÷320°C and this is a transformation of the retained austenite. As the result of this transformation, a non-homogeneous mixture consisting of supersaturated ferrite and cementite, i.e. lower bainite forms [1, 2, 4]. Cementite is formed during the third transformation occurring during tempering in the temperature range of 200÷420°C. This results in further decarbonization of the matrix and dissolution of metastable ε carbides allowing for the recovery of the steel matrix [4, 7]. The mechanism of the nucleation of cementite is, however, not fully understood yet. According to Ref. [4] precipitating cementite nucleates independently or in situ on ε carbide particles. Whereas according to Ref. [5] cementite nucleates independently, mainly on grain boundaries of former austenite or on subgrain boundaries of the newly formed cell structure. Above 400°C diffusion of alloying elements such as V, Mo and W takes place. Then, the cementite gradually dissolves to make the nucleation of MC and M2C carbides coherent with the alloy matrix possible. This leads to an [...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 52655 "Kinetics of phase transfo..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2010-3 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2010-3

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma