Shrinkage of alkali-activated slag-fly ash concrete cured at ambient temperature

Skurcz betonu z aktywowanym alkalicznie spoiwem żużlowo-popiołowym pielęgnowanego w temperaturze otoczenia

10.15199/33.2024.08.01

nr katalogowy: 150122
10.15199/33.2024.08.01

Streszczenie

The paper summarizes the results of a study intended to characterize alkali-activated slag/fly ash concretes concerning their volume changes, freeze-thaw resistance, scaling resistance, and alkali-aggregate reactivity. The manifestation of early-age microcracking in the hardened alkali-activated paste phase of these concretes calls for attention. It is related to significant autogenous shrinkage, although it does not appear to agree with the other shrinkagemeasurements performed in the experimental program. Smaller pores and high sodiumion concentration result in higher internal pressure during the process of self-desiccation and could be the main causes for the very high autogenous shrinkage values recorded.

Abstract

W artykule przedstawiono wyniki badań betonu z alkalicznymspoiwemżużlowo-popiołowym. Oznaczono zmianę objętości, odporność na cykle zamrażania-rozmrażania, w tym na złuszczanie, oraz reaktywność alkaliczno-krzemianową. Zwrócono uwagę na występowanie mikropęknięć w stwardniałym zaczynie we wczesnymwieku.Wysunięto hipotezę, że jest to związane ze znacznymskurczemautogenicznym, jakkolwiek inne pomiary skurczu, przeprowadzonewprogramie badawczym, nie potwierdzają tego mechanizmu. Małe pory i duże stężenie jonów sodu powodują wysokie ciśnienie wewnętrzne podczas wysychania imogą być głównymi przyczynami dużych wartości skurczu autogenicznego zarejestrowanych w badaniach.

Słowa kluczowe

Keywords

Bibliografia

[1] McLellan BC, Williams RP, et al. Costs and carbon emissions for geopolymer pastes in comparison to ordinary portland cement. J. of Clean. Prod. 2011; 19(9-10): 1080 – 1090.
[2] BernalSA,MejíaDeGutiérrezR., et al.Effectofbinder content on the performance of alkali-activated slag concretes. Cem. and Conc. Res. 2011; 41 (1): 1 – 8.
[3] FangG,HoWK, et al.Workability andmechanical properties of alkali-activated fly ash-slag concrete cured at ambient temperature. Construction and BuildingMaterials. 2018; 172: 476–487.
[4] MaY,Ye G. The shrinkage of alkali activated fly ash. Cem. and Conc. Res. 2015; 68: 75–82.
[5] Rodrigue A. Optimisation et durabilité des écobétons alcali-activés incorporant des laitiers de haut- -fourneau et des cendres volantes, Ph.D. Thesis, Laval University, Québec (Canada). 175 p.
[6] Rodrigue,A.,Bissonnette, et al.,Shrinkage of alkaliactivated combined slag and fly ash concrete cured at ambient temperature,ACIMat. J., 119(3), 15-23 (2022).
[7] Provis JL,MyersR. J et al.:X-raymicrotomography shows pore structure and tortuosity in alkali-activated binders. Cem. and Conc. Res. 2012; 42 (6): 855 – 864.
[8] Gao X,Yu QL et al.:Assessing the porosity and shrinkage of alkali activated slag-fly ash composites designed applying a packing model. Const. and Build. Mat. 2016; 119: 175 – 184.
[9] Ballekere Kumarappa D, Peethamparan S et al.: Autogenous shrinkage of alkali activated slag mortars: Basic mechanisms and mitigation methods. Cem. and Conc. Res., 109, 1–9 (2018).
[10] Ye H, Radlińska A. Fly ash-slag interaction during alkaline activation: Influence of activators on phase assemblage and microstructure formation. Const. and Build. Mat. 2016; 122: 594–606).
[11] Bernal SA, Provis JL et al. Gel nanostructure in alkali-activated binders based on slag and fly ash, and effects of accelerated carbonation. Cem. and Conc. Res. 2013; 53: 127 – 144.
[12] Rodrigue A, Duchesne J et al. Influence of added water andflyashcontentonthe characteristics,properties and early-age cracking sensitivity of alkali-activated slag/flyashconcretecuredatambient temperature.Const. and Build.Mat. 2018; 171: 929 – 941.
[13] Provis JL, vanDeventer JSJ.AlkaliActivatedMaterials. RilemState-of-the-ArtReports, Springer. 2014.

Publikacja


e-Publikacja (format pdf) - nr 42511 "Health Safety of Material..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OPAKOWANIE - e-zeszyt (pdf) 2009-I licencja: Osobista Produkt cyfrowy	19.50 zł

Prenumerata

OPAKOWANIE - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

234.00 zł

OPAKOWANIE - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OPAKOWANIE - papierowa prenumerata roczna	300.00 zł brutto 277.78 zł netto 22.22 zł VAT (stawka VAT 8%)
OPAKOWANIE - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

342.00 zł

OPAKOWANIE - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OPAKOWANIE - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	360.00 zł brutto 333.33 zł netto 26.67 zł VAT (stawka VAT 8%)

360.00 zł

Open Access

Zeszyt

2024-8

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma