Microstructural and Mechanical Characterization of Spot Welds on AISI 430 ferritic stainless steel sheets

Mikrostrukturalna i mechaniczna charakterystyka zgrzein punktowych na ferrytycznych blachach ze stali nierdzewnej AISI 430

10.15199/48.2024.06.61

nr katalogowy: 149023
10.15199/48.2024.06.61

Streszczenie

Electric resistance spot welding is a simple and fast process that is widely applied on stainless steel sheets. During this process, a high electric current flows between the electrodes through the pressure parts. By the Joule effect, a nugget of molten solder is formed between the welded parts. In this study, AISI 430 ferritic stainless steel sheets were spot welded by electrical resistance with different welding parameters. The effect of the welding current and the holding time during welding on the microstructure and the mechanical properties of the welded joints have been investigated. Tensile tests and micro hardness measurements were carried out to assess the mechanical properties and the breaking characteristics of the welded joints. The obtained results show that the nugget size, the tensile strength of the welded sheets and the micro hardness distribution depend on the welding parameters. The micro structural study allowed us to explain the transformations produced during welding

Abstract

Zgrzewanie punktowe oporem elektrycznym jest prostym i szybkim procesem, który jest szeroko stosowany w przypadku blach ze stali nierdzewnej. Podczas tego procesu pomiędzy elektrodami poprzez części ciśnieniowe przepływa duży prąd elektryczny. Dzięki efektowi Joule'a pomiędzy spawanymi częściami tworzą się bryłki stopionego lutowia. W tym badaniu arkusze ferrytycznej stali nierdzewnej AISI 430 zostały zgrzane punktowo za pomocą opornika elektrycznego przy różnych parametrach spawania. Badano wpływ prądu spawania i czasu przetrzymywania podczas spawania na mikrostrukturę i właściwości mechaniczne złączy spawanych. W celu oceny właściwości mechanicznych i wytrzymałości złączy spawanych przeprowadzono próby rozciągania oraz pomiary mikrotwardości. Uzyskane wyniki pokazują, że wielkość bryłki, wytrzymałość na rozciąganie zgrzewanych blach oraz rozkład mikrotwardości zależą od parametrów zgrzewania. Badania mikrostrukturalne pozwoliły wyjaśnić przemiany powstałe podczas spawania.

Słowa kluczowe

Keywords

Bibliografia

[1] Amuda, Moh, and S. Mridha. "Microstructural features of AISI 430 ferritic stainless steel (fss) weldproduced under varying proc."International Journal of Mechanical and Materials Engineering4, no. 2 (1970)
[2] S. Zaman, M. A. Khattak, and M. N. Tamin, “AkademiaBaru Effects of Welding on the Microstructural Properties of AISI 430 Ferritic Stainless Steel AkademiaBaru,” vol. 1, no. 1, pp. 25–32, 2018.
[3] Amuda MOH, Mridha S. Microstructural features of AISI 430 ferritic stainless steel weld produced under varying process parameters. International Journal of Mechanical and Materials Engineering.2009; 4:160-166.
[4] C. N. Gonçalves, G. Mendes, D. A. Carvalho, J. S. Siqueira, and R. Â. Renzetti, “Influence of Nb Content on Sensitization and Pitting Corrosion of Welded AISI 430 Ferritic Stainless Steel,” vol. 6973, pp. 1–10, 2019.
[5] J.R. Davis, B.R. Sanders (Eds.), Welding, Brazing and Soldering, Metals Handbook, ninth ed., vol. 6, American Society for Metals, Metals Park, OH, 1983, pp. 525–534.
[6] A. Standard, “E407-07: StandardPractice for Micro-etching Metals and Alloys,”ASTM Int. West Conshohocken, PA, vol.11, November,pp.1–21, 2012.
[7] Z. Al, M. Si, A. Coated, and S. Sheets, “Welding of SuperDyma,” 2012.
[8] M. Alizadeh-Sh, S. P. H. Marashi, and M. Pouranvari, “Resistance spot welding of AISI 430 ferritic stainless steel: Phase transformations and mechanical properties,” Mater. Des., vol. 56, pp. 258–263, 2014,
[9]M. Pouranvari, “On the failure mode of resistance spot welded HSLA 420 steel,” Arch. Metall. Mater., vol. 58, no.1, pp.67–72, 2013, doi: 10.2478/v10172-012-0152y.
[10] M. Pouranvari and S. P. H. Marashi, “Welding metallurgy of stainless steels during resistance spot welding Part I : fusion zone,” vol. 20, no. 6, pp. 502–511, 2015, doi: 10.1179/1362171815Y.0000000015.
[11] Jamasri MN, Ilman R, Soekrisno,Triyono. Corrosion Fatique Behaviour of RSW Dissimilar Metal Welds Between Carbon Steel and Austenitic Stainless Steel with Different Thickness. Procedia Engineering, 10: 649-654. 2011.
[12] N. Charde, “Spot Weld Growth on 304L Austenitic Stainless Steel for Equal and Unequal Thicknesses,” Casp. J. Appl. Sci. Res., vol. 1, no. 11, pp. 83–91, 2012.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


PRZEGLĄD ELEKTROTECHNICZNY- e-publikacja (pdf) z zeszytu 2024-6 , nr katalogowy 149023 licencja: Osobista Produkt cyfrowy Nowość	10.00 zł

Zeszyt


PRZEGLĄD ELEKTROTECHNICZNY- e-zeszyt (pdf) 2024-6 licencja: Osobista Produkt cyfrowy Nowość	85.00 zł

Prenumerata

PRZEGLĄD ELEKTROTECHNICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEGLĄD ELEKTROTECHNICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Zeszyt

2024-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma