Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2023 - zeszyt 8

Evaluating the causes of damage to corrosion protection coatings on lightning protection masts of a 400 kV substation

Ocena przyczyn uszkodzeń powłok antykorozyjnych na słupach odgromowych stacji 400 kV

10.15199/40.2023.8.2

nr katalogowy: 144538
10.15199/40.2023.8.2

Streszczenie

A polyvinyl anti-corrosion coating system used to protect the lightning masts installed at a 400 kV substation showed significant damage after three years of operation. Field tests (measurements of thickness, adhesion, continuity using the low-voltage method, and the appearance of the coatings was assessed using a field microscope) and laboratory tests (infrared spectroscopy, examination of the morphology and elemental composition of the coatings under a scanning microscope with an EDX attachment) were carried out on collected samples. Degradation of the organic part of the protection was observed. Local exposure of the coatings to high temperatures was likely the cause of the damage.

Abstract

Poliwinylowy powłokowy system antykorozyjny zastosowany na słupach odgromowych stacji 400 kV uległ znacznemu zniszczeniu po trzech latach eksploatacji. Wykonano badania polowe (pomiary grubości, przyczepności, szczelności metodą niskonapięciową, oceniono wygląd powłok przy użyciu mikroskopu polowego) oraz badania laboratoryjne na pobranych próbkach (spektroskopię w podczerwieni, badania morfologii i składu pierwiastkowego powłok pod mikroskopem skaningowym z przystawką EDX). Stwierdzono degradację organicznej części zabezpieczeń. Przyczyną zniszczeń było prawdopodobnie miejscowe oddziaływanie na powłoki wysokiej temperatury

Słowa kluczowe

Keywords

Bibliografia

[1] T. da Silva Lopes, T. Lopes, D. Martins, C. Carneiro, J. Machado, A. Mendes. 2020. “Accelerated Aging of Anticorrosive Coatings: Two-Stage Approach to the AC/DC/AC Electrochemical Method.” Progress in Organic Coatings 138: 105365. DOI: 10.1016/j.porgcoat.2019.105365.
[2] K. N. Allahar, G. P. Bierwagen, V. Johnston Gelling. 2010. “Understanding AC– DC–AC Accelerated Test Results.” Corrosion Science 52(4): 1106–1114. DOI: 10.1016/j.corsci.2009.12.001.
[3] Bo Tao, Li Cheng, Jiuyi Wang, Xinlong Zhang, Ruijin Liao. 2022. “A Review on Mechanism and Application of Functional Coatings for Overhead Transmission Lines.” Frontiers in Materials 9: 995290. DOI: 10.3389/fmats.2022.995290.
[4] Hao Liu, Fei Lu, Peijie Liu, Manping Luo. 2020. “Design of Anti-Rust Scheme of Transmission Tower Based on the Distribution Characteristics of Rust Factor.” IEEE 1st China International Youth Conference on Electrical Engineering (CIYCEE). Wuhan, China. DOI: 10.1109/CIYCEE49808.2020.9332743.
[5] Working Group B2.44. 2015. Coatings for Protecting Overhead Power Network Equipment in Winter Conditions. Paris: CIGRÉ.
[6] V. Nagda. Corona Discharge in Power Transmission Lines. https:// instrumentationtools.com/corona-discharge-in-power-transmissionlines/?utm_content=cmp-true (access: 30.05.2023).
[7] Fan Zhang, Pengfei Ju, Mengqiu Pan, Dawei Zhang, Yao Huang, Guoliang Li, Xiaogang Li. 2018. “Self-Healing Mechanisms in Smart Protective Coatings: A Review.” Corrosion Science 144: 74–88. DOI: 10.1016/j. corsci.2018.08.005.
[8] P. A. Sørensen, S. Kiil, K. Dam-Johansen, C. E. Weinell. 2009. “Anticorrosive Coatings: A Review.” Journal of Coatings Technology and Research 6(2): 135– 176. DOI: 10.1007/s11998-008-9144-2.
[9] R. B. Seymour, H. F. Mark (eds.). 1990. Organic Coatings: Their Origin and Development: Proceedings of the International Symposium on the History of Organic Coatings, Held September 11–15, 1989, in Miami Beach, Florida, USA. New York: Elsevier.
[10] S. B. Ulaeto, R. P. Ravi, I. I. Udoh, G. M. Mathew, T. P. D. Rajan. 2023. “Polymer- -Based Coating for Steel Protection, Highlighting Metal-Organic Framework as Functional Actives: A Review.” Corrosion and Materials Degradation 4(2): 284–316. DOI: 10.3390/cmd4020015.
[11] S. B. Lyon, R. V. Bingham, D. J. Mills. 2017. “Advances in Corrosion Protection by Organic Coatings: What We Know and What We Would Like to Know.” Progress in Organic Coatings 102: 2–7. DOI: 10.1016/j.porgcoat. 2016.04.030

Zeszyt


OCHRONA PRZED KOROZJĄ- e-zeszyt (pdf) 2023-8 licencja: Osobista Produkt cyfrowy Nowość	45.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Open Access

Zeszyt

2023-8

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma