Evaluation of 13MnSi6-5 TRIP steel mechanical properties determined in the impact tensile test

Ocena właściwości mechanicznych stali 13MnSi6-5 wyznaczonych w próbie dynamicznego zrywania

10.15199/28.2019.6.2

Adam Kokosza

nr katalogowy: 124110
10.15199/28.2019.6.2

Streszczenie

The results of the research of mechanical properties, obtained under dynamic loads by impact tensile tests, are presented and discussed in this paper. Based on the obtained results the sensitivity of the investigated 13MnSi6–5 TRIP steel to the loading rate was found. This sensitivity manifested itself by higher values of the strength and plasticity than values obtained in the static tests. A high tendency of the investigated steel to the increase of the deformation resistance in the initial stage of its dynamic loading was also stated. A distinct effect of the heat treatment on the basic mechanical properties, determined under conditions of the dynamic loading, was also shown in the hereby paper.

Abstract

Celem badań było wyznaczenie podstawowych właściwości dynamicznych niskowęglowej stali typu TRIP w warunkach dynamicznego zrywania. Na podstawie uzyskanych wyników podjęto również próbę oceny wpływu wybranych parametrów obróbki cieplnej na uzyskane właściwości mechaniczne.

Słowa kluczowe

Keywords

Bibliografia

[1] Grajcar A., Kuziak R., Zalecki W.: Third generation of AHSS with increased fraction of retained austenite for the automotive industry. Archives of Civil and Mechanical Engineering 12 (3) (2012) 334÷341.
[2] Galan J., Samek L., Verleysen P., Verbeken K., Houbaert Y.: Advanced high strength steels for automotive industry. Revista de Metalurgia A 48 (2) (2012) 118÷131.
[3] Grajcar A., Kwaśny W., Zalecki W.: Microstructure-property relationships in TRIP aided medium-C bainitic steel with lamellar retained austenite. Materials Science and Technology 31 (7) (2015) 781÷794.
[4] Schmitt J. H., Iung T.: New developments of advanced high-strength steels for automotive applications. Comptes Rendus Physique 19 (8) (2018) 641÷656.
[5] Li J., Zhang J., Li Q., Guo D., Liu Y., Meng Q.: The effect of an austenitizing pretreatment on the morphology and distribution of the retained austenite and mechanical properties of TRIP590 steel. Journal Of Materials Science 53 (22) (2018) 15667÷15678.
[6] Salinas A., Artigas A., Perez-Ipiña J., Castro-Cerda F., Garza-Montes-de- Oca N., Colás R., Petrov R., Monsalve A.: Effects of heat treatment on morphology, texture, and mechanical properties of a MnSiAl multiphase steel with TRIP behavior. Metals 8 (12) (2018) doi:10.3390/met8121021.
[7] Huh H., Lim J. H., Park S. H.: High speed tensile test of steel sheets for the stress-strain curve at the intermediate strain rate. International Journal of Automotive Technology 10 (2) (2009) 195÷204.
[8] Huh H., Seok-Bong K., Jung-Han S., Ji-Ho L.: Dynamic tensile characteristics of TRIP-type and DP-type steel sheets for an auto-body. International Journal of Mechanical Sciences 50 (5) (2008) 918÷931.
[9] Huh H., Jeong S., Bahng G. W., Chae K.S., Kim C.G.: Standard uncertainty evaluation for dynamic tensile properties of auto-body steel-sheets. Experimental Mechanics 54 (6) (2014) 943÷956.
[10] Grajcar A.: Odkształcanie dynamiczne elementów z wysokowytrzymałych stali wielofazowych dla motoryzacji. Stal, Metale & Nowe Technologie 5-6 (2015) 80÷84.
[11] Pacyna J., Kokosza A.: Kinetyka przemian fazowych przechłodzonego austenitu stali Mn-Si chłodzonych z zakresu temperatur krytycznych. Inżynieria Materiałowa 33 (5) (2012) 386÷391.
[12] Kokosza A.: Kształtowanie mikrostruktury niskowęglowej stali typu TRIP podczas wyżarzania w zakresie temperatur krytycznych. Inżynieria Materiałowa 35 (1) (2014) 19÷24.
[13] Kokosza A., Pacyna J., Dziurka R.: Kinetyka przemian przechłodzonego austenitu stali 13MnSi6-5 typu TRIP chłodzonej z zakresu temperatur krytycznych. Inżynieria Materiałowa 36 (5) (2015) 324÷328.
[14] Kokosza A.: Mikrostruktura i własności stali typu TRIP po niekonwencjonalnym wyżarzaniu w zakresie temperatur krytycznych. Mat. Konf. XLVI Szkoły Inżynierii Materiałowej Rytro September 25th÷28th (2018) 14÷21.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 124110 "Evaluation of 13MnSi6-5 T..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2019-6 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2019-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma