Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2016 - zeszyt 4

Effect of the powder consolidation with biopolymer on the corrosion characteristics of bonded magnets based on Nd-(Fe,Co)-B

10.15199/40.2016.4.8

nr katalogowy: 97716
10.15199/40.2016.4.8

In this paper the effect of the Nd-(Fe,Co)-B powder particles consolidation process with difrent types of organic resin on the corrosion resistance of the bonded magnets in the aggressive environments was presented. The tests were carried out on the magnetic material based on Nd12Co5Fe77B6 powder consolidated with two types of resin (termo-setting epoxy resin and chemicalsetting biopolymer). Impact of the used consolidation process was rated on the basis of polarization curves recorded in: sulphate enviroment (pH = 3), phosphate enviroment (pH = 3), as well as in phosphate environment with chloride ions (Cl-) and Ringer solution (pH = 6) assigned during electrochemical measurements of polarization resistance. It has been found that the consolidation of powder particles with biopolimer has a beneficial effect on the corrosion resistance of the final magnetic material. Keywords: bonded magnets, corrosion resistance, consolidation process, biopolymer Wpływ konsolidacji biopolimerem na charakterystyki korozyjne wiązanych magnesów Nd-(Fe,Co)-B W artykule przedstawiono wpływ procesu konsolidacji cząstek proszku Nd-(Fe,Co)-B różnymi typami żywic organicznych na odporność korozyjną wiązanych magnesów w środowiskach agresywnych. Do badań posłużono się wiązanymi materiałami magnetycznymi na bazie proszku Nd12Co5Fe77B6 wiązanych dwoma rodzajami spoiwa (termoutwardzalna żywica epoksydowa i chemoutwardzalny biopolimer).Wpływ procesu konsolidacji żywicami organicznymi oceniono na podstawie badań elektrochemicznych w środowisku: siarczanowym (pH = 3), fosforanowym (pH = 3), w fosforanowym z dodatkiem jonów chlorkowych (Cl-) oraz w roztworze Ringera (pH = 6). Stwierdzono, że proces konsolidacji proszku biopolimerem korzystnie wpływa na odporność korozyjną finalnego materiału magnetycznego. Słowa kluczowe: magnesy wiązane, odporność korozyjna, proces konsolidacji, biopolimer.1. Introduction Magnetic materials occupy very important position in many areas [...]

Bibliografia

[1] Biesaga R. 2005. "Protezy całkowite oraz protezy overdenture". Protetyka stomatologiczna w teorii i praktyce Łódź: Wydawnictwo Bestom.
[2] Chung R., A. Siu, F. Chu, T. Chow. 2003. "Magnet-retained auricular prosthesis with an implant supported composite bar: a clinical report". J. Prosthet. Dent. Vol. 89 : 446-49.
[3] Domański W. 2004. "Dianowe żywice epoksydowe - zagrożenia czynnikami chemicznymi". Bezpieczeństwo pracy 9: 16-20.
[4] Fujimoto T., A. Niimi, I. Murakami, M. Ueda, J. Oral. 1998. "Use of new magnetic attachments for implant-supported overdentures". Implantol. 24 : 147-51.
[5] Górecki A. 1984. Technologia ogólna - podstawy technologii mechanicznej. Warszawa: WSiP.
[6] Herzer G., M. Verquez, M. Knobel, A. Zhukov, T. Reininger, H. A. Davies, R. Grössinger, J. L. Sanchez.2005. "Round table discussion: present and future applications of nanocrystalline magnetic materials". J. Magn. Magn. Mater. 294 : 252-266.
[7] Klimecka D., G. Pawłowska, M. Sozańska. 2015. "The effect of powder particles biencapsulation with Ni-P layer on local corrosion of bonded Nd- (Fe, Co)-B magnetic material". Archives of Metallurgy and Materials. Vol. 60 (1) : 153-157.
[8] Klimecka -Tatar D., G. Pawłowska, K. Radomska. 2013. "Effect of the Nd- (Fe,Co)-B powder biencapsulation with Ni-P/epoxy resin and phosphate/ epoxy resin coatings on the potentiokinetic characteristic of bonded magnets in the phosphate solution", Ochrona przed Korozją 5 : 187-190.
[9] Klimecka-Tatar D. 2014."The powdered Magnets Technology Improvement by Biencapsulation Method and Its Effect on Mechanical Properties". Manufacturing Technology .Vol. 14 nr 1: 30-36.
[10] Koczorowski R., R. Brożek, M. Hemerling. 2006. "Wykorzystanie elementów precyzyjnych w leczeniu implantoprotetycznym". Dent. Med. Probl. 43 : 421-428.
[11] Lachowicz H. 1997. "Magnetyki amorficzne". Wyd. Wiedzy i Życia nr 9.
[12] Langot C., M. I. Pers, M. Janicki. 2004. "Wykorzystanie systemu retencji magnetycznej Dyna w protetycznej rehabilitacji pacjenta". Prot Stomat. 54 : 100.
[13] Leonowicz M. J. Wysłocki. 2005. Współczesne magnesy. Warszawa: WNT.
[14] Machnikowski, J. Gładkowski, M. Siedlecki, T. Feder. 2002. "Zastosowanie precyzyjnych elementów retencyjnych u pacjentów z rozległymi brakami zębowymi". Prot. Stomat. 52 : 344-348.
[15] Meada Y., K. Nakao, K. Yagi, S. Matsuda. 2006. "Composite resin root coping with a keeper for magnetic attachment for replacing the missing coronal portion of a removable partial denture abutment". J. Prosthet. Dent. Vol. 96 : 139-142.
[16] Pawłowska G., D. Klimecka-Tatar, S. Szymura. 2010. "Enkapsulacja jako skuteczny sposób zapobiegania utlenianiu proszków w technologii magnesów wiązanych". Ochr. przed Koroz. 11 : 585-588.
[17] Pawłowska G., D. Klimecka-Tatar, A. Mazik. 2013. "Wpływ bienkapsulacji proszków Nd12Fe77Co5 B6 na kinetykę roztwarzania materiałów wiązanych w zakwaszonych roztworach siarczanowych". Hutnik. 5 : 398-403.
[18] Pawłowska G. 2011. Procesy korozyjne materiałów magnetycznych typu RE-Fe-B otrzymanych różnymi metodami. Częstochowa: Monografia Nr 10.
[19] Punjani S., A. Arora, V. Upadhyaya. 2012. "Subway Mandibular Buccal Defect Blocked with Two Part Prosthesis Unified by Earth Magnets". J Indian Prosthodont Soc., Springer 13 (1) : 56-60.
[20] Radomska K., G. Pawłowska, D. Klimecka-Tatar.2015. "The corrosion processes effect on surface roughness of bonded magnetic material based on Nd-(Fe,Co)-B powder", Solid State Phenomena, vol. 227 : 39-42.
[21] Spiechowicz E.2008. "Protetyka Stomatologiczna". Warszawa: Wyd. Lek. PZWL.
[22] Stendera P., P. Grochowski. 2010. "Natychmiastowa proteza typu overdenture na implantach w żuchwie". Protet. Stomatol. LX 6 : 479-483.
[23] Ślusarek B., I. Dudzikowski. 2002. "Application of permanent magnets made from NdFeB powder and from mixtures of powders in DC motors". J. Magn. Magn. Mater. 239 : 597.
[24] Ślusarek B.2001. Dielektromagnesy Nd-Fe-B. Wrocław: Politechnika Wrocławska.
[25] Tomizuka R., H. Kanetaka, Y. Shimizu, A. Suzuki, K. Igarashi. 2005. International Congress Series. 1284 : 322.
[26] Walmsley AD, CL Brady, PL Smith, JW Frame. 1993. "Magnet-retained overdentures using the Astra dental implant system". Br Dent J. 174 (4) : 399-404.
[27] Więckiewicz W., M. Bartczyszyn, J. Maczura-Sokalska. 2009. Protet. Stomatol. 6 : 423.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 120469 "Minimization of Objective..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2019-6 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEGLĄD ELEKTROTECHNICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEGLĄD ELEKTROTECHNICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Zeszyt

2016-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma