Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2018 - zeszyt 2

Characterization of magnesium LAE442 alloy microstructure after deformation process with the use of KoBo method

Charakterystyka mikrostruktury stopu magnezu LAE442 po procesie odkształcenia metodą KoBo

10.15199/28.2018.2.2

Iwona Bednarczyk

nr katalogowy: 113383
10.15199/28.2018.2.2

Streszczenie

At present, there is a growing demand of the aviation industry on the parts prepared from light alloys which are characterised with sufficient stiffness and resistance. The technology of plastic deformation of magnesium alloys is a huge challenge. Due to the low plasticity of those materials in room temperature the parameters of the process of plastic working must be a satisfying compromise between the cost and the quality of the products. Due to those facts, alternative methods of plastic deformation of magnesium alloys need to be found. Particularly promising results in terms of the improvement in the susceptibility to plastic deformation are brought by new ultra-light magnesium alloys containing lithium. With the introduction of lithium, the density of which is 0.535 g/cm3, into the chemical composition of alloy, a further decrease of weight of alloy is achieved but at the same time the resistance of the material decreases. The article presents the results of tests of plastic deformation of Mg–Li–RE magnesium alloys. Alloys for extrusion process were achieved with the method of vacuum melting and casting to graphite moulds. The materials for tests were cast slabs from magnesium alloys with symbols LAE442. Before the process of deformation the castings were subject to homogenization. The tests of extrusion were conducted in complex state of deformation with using KOBO method. An assessment was performed of the influence of deformation process parameters on the microstructure of tested alloy. An analysis of microstructure was conducted both in initial condition and condition after plastic deformation with the use of techniques of light and scanning transmission electron microscopy.

Abstract

Obecnie obserwuje się rosnące zapotrzebowanie przemysłu lotniczego na części wykonane ze stopów magnezu, które spełnią określone wymagania wytrzymałościowe. Jednak mała plastyczność stopów magnezu w temperaturze pokojowej powoduje, że są poszukiwane alternatywne sposoby kształtowania tej grupy materiałów. Szczególnie obiecujące w zakresie poprawy podatności do kształtowania plastycznego są nowe ultralekkie stopy magnezu zawierające w swoim składzie chemicznym lit. W artykule przedstawiono wyniki analizy mikrostruktury prętów otrzymanych ze stopu LAE442 po procesie odkształcenia metodą KoBo. Określono zmiany powstałe w mikrostrukturze stopu LAE442 po odkształceniu plastycznym metodą KoBo.

Słowa kluczowe

Keywords

Bibliografia

[1] Białobrzeski A., Saja K., Hubner K.: Ultra-light magnesium-lithium alloys. Archives of Foundry Engineering 7 (2007) 11÷16.
[2] Białobrzeski A., Lech-Grega M., Żelechowski J.: Structure tests of magnesium and lithium alloys with two-phase α-β and single-phase β structure. Papers of the Foundry Institute 1 (2010) 17÷28.
[3] ASM Binary alloy phase diagrams. 1996 ASM International.
[4] Białobrzeski A., Saja K., Hübner K.: Ultra-light alloys Mg-Li. Foundry Journal of the Polish Foundrymen’s Association 59 (2009) 276÷288.
[5] Hadasik E., Kuc D., Niewielski G., Śliwa R.: Development of magnesium alloys for plastic working. Metallurgical News 8 (2009) 580÷584.
[6] Dutkiewicz J., Rusz S., Maziarz W., Skuza W., Kuc D., Hilser O.: Modification of microstructure and properties of extruded Mg-Li-Al alloys of α and α + β phase composition using ECAP processing. Acta Phys. Pol. A 131 (2017) 1303÷1306.
[7] Szala J.: Application of computer picture analysis methods to quantitative assessment of structure in materials. Scientific Journals of Silesian University of Technology. Series Metallurgy. Gliwice (2008).
[8] Mikuszewski T.: Melting and casting of ingots from made of Mg-Li types alloys. Metalurgija 53 (2014) 588÷590.
[9] Bochniak W.: Theoretical and practical aspects of plastic shaping of metals with the use of KoBo method. Publishing house of AGH, Kraków (2009).
[10] Bochniak W., Korbel A., Ostachowski P., Ziółkiewicz S., Borowski J.: Extrusion of metals and alloys with the use of KoBo method. Plastic Processing of Metals XXIV 2 (2013) 83÷97.
[11] Korbel A., Bochniak W., Borowski J., Błaż L., Ostachowski P., Łagoda M.: Anomalies in precipitation hardening process of 7075 aluminium alloy extruded by KOBO method. J. Mater. Process Tech. 216 (2015) 160÷168.
[12] Witte F., Fischer J., Nellesen J., Vogt C., Vogt J., Donath T.: In vivo corrosion and corrosion protection of magnesium alloy LAE442. Acta Biomater. 6 (2010) 1792÷1799.
[13] Bednarczyk I., Kuc D., Tomaszewska A., Mrugała A.: The influence of extrusion process on the microstructure and mechanical properties of magnesium alloys. Arch. Metall. Mater. 62 (2017) 545÷550.
[14] Bednarczyk I., Mrugała A., Tomaszewska A.: Influence of plastic deformation process on the structure and properties of alloy WE43. Arch. Metall. Mater. 61 (2016) 389÷392.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 113383 "Characterization of magne..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2018-2 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2018-2

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma