Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2018 - zeszyt 1

Effect of metallurgical factors on steel pipe corrosion in water distribution systems

Wpływ czynników metalurgicznych na korozję rur stalowych w systemach dystrybucji wody

10.15199/28.2018.1.6

nr katalogowy: 112403
10.15199/28.2018.1.6

Streszczenie

Traditional metallography combined with microhardness testing and chemical composition analysis were used to understand the premature deterioration of steel pipes used in water distribution systems, namely, a zinc-coated steel pipe used in potable water distribution systems and a black steel pipe used for sprinkler fire protection systems. The investigated pipes were found to fail after a short service time, with numerous water leaks in a period of less than two years of service. This study shows that the failure was mainly a consequence of the Sandelin phenomenon caused by inadequate metallurgical quality, i.e. the silicon content was too high in the zinc-coated steel pipe, and an improper seam welding procedure in the case of the black steel pipes.

Abstract

Przyczyn perforacji korozyjnych rur stalowych w systemach dystrybucji wody należy upatrywać się w wielu czynnikach. Najczęstszym czynnikiem jest nadmierna agresywność korozyjna wody pitnej, zwłaszcza w przypadku rur stalowych ocynkowanych. W niektórych przypadkach bezpośrednią przyczyną wystąpienia perforacji korozyjnych jest odwrócenie polaryzacji w układzie powłoka cynkowa–stal na skutek zbyt wysokiej temperatury wody z powodu wykonywania operacji termicznego usuwania bakterii Legionella. Nie należy jednak zapominać o kontrolowaniu jakości metalurgicznej stosowanych rur stalowych. Celem pracy było określenie przyczyn przedwczesnych perforacji korozyjnych w rurach stalowych ze szwem liniowym czarnych (powszechnie stosownych w systemach tryskaczy ppoż.), jak i rurach stalowych ocynkowanych, stosowanych w systemach dystrybucji wody zimniej i ciepłej. Przeprowadzono badania makroskopowe oraz metalograficzne obszaru zgrzewu i materiału rodzimego. Wyznaczono profil mikrotwardości obszaru zgrzewu dla obu badanych rur.

Słowa kluczowe

Keywords

Bibliografia

[1] McNeill L. S., Edwards M.: Review of iron pipe corrosion in drinking water distribution systems. American Water Works Association 93 (2001) 88÷100.
[2] Volk C., Dundore E., Schiermann J., Lechevallier M.: Practical evaluation of iron corrosion control in a drinking water distribution system. Water Research 34 (2000) 1967÷1974.
[3] Della Rovere C. A., Silva R., Moretti C., Kuri S. E.: Corrosion failure analysis of galvanized steel pipes in a water irrigation system. Engineering Failure Analysis 33 (2013) 381÷386.
[4] Slavíčková K., Grünwald A., Šťastný B.: Monitoring of the corrosion of pipes used for the drinking water treatment and supply. Civil Engineering and Architecture 1 (2013) 61÷65.
[5] Pawłowski B., Krawczyk J., Bała P.: The premature deterioration of zinccoated steel pipes in water distribution system. International Journal of Material and Mechanical Engineering 2 (2013) 43÷47.
[6] Delaunois F., Tosar F., Vitry V.: Corrosion behaviour and biocorrosion of galvanized steel water distribution systems. Bioelectrochemistry 97 (2014) 110÷119.
[7] Orlikowsk J., Ryl J., Jazdzewska A., Krakowiak S.: Effect of thermal shock during legionella bacteria removal on the corrosion properties of zinc-coated steel pipes. Journal of Materials Engineering and Performance 25 (2016) 2711÷2719.
[8] Goritsky V. M., Goritsky O. V., Dourneva A. A., Shneiderov G. R.: Special features of corrosion-mechanical damage in welded joints of in the main heating system of moscow. Welding International 28 (2014) 738÷743.
[9] Foct J., Reumont G., Dupont G., Perrot P.: How does silicon lead the kinetics of the galvanizing reaction to lose its solid-solid character. Journal de Physique IV 3 (1993) 961÷966.
[10] Kopyciński D., Guzik E., Wołczyński W.: The zinc coating solidification on surface silicon steels and DI castings. Inżynieria Materiałowa 3 (2010) 328÷331.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 112403 "Effect of metallurgical f..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2018-1 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2018-1

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma