Corrosion properties of Ni/Al2O3/Cgraphite hybrid composite layers

Właściwości korozyjne hybrydowych warstw kompozytowych Ni/Al2O3/Cgrafit

10.15199/40.2018.2.2

nr katalogowy: 112186
10.15199/40.2018.2.2

Streszczenie

The paper presents the results of studies of composite layers with nickel matrix and dispersed phase in the form of: alumina oxide (Al2O3) and graphite (Cgraphite) produced by electrodeposition on steel substrate. Three variants of composite layers were produced: Ni/Al2O3, Ni/Cgraphite, Ni/Al2O3/Cgraphite and for comparison purpose a nickel layer was also produced. Alumina oxide and graphite powders were used as dispersion phases. The dispersed phases were characterized by scanning electron microscopy (SEM) and Raman spectroscopy for graphite powder. The results of investigations of the structures of the produced layers with SEM, EDS, and results of Vickers hardness measurements as well as results of corrosion tests using electrochemical potentiodynamic method are presented. Damage characteristics after corrosion studies were obtained using a light microscope.

Abstract

W pracy przedstawiono wyniki badań warstw kompozytowych z niklową osnową oraz wbudowanymi w nią cząstkami faz dyspersyjnych w postaci: tlenku glinu (Al2O3) oraz grafitu (Cgrafit) wytwarzanych w procesie elektroosadzania na podłożu stalowym. Wytworzono trzy warianty powłok kompozytowych: Ni/Al2O3, Ni/Cgrafit, kompozytową warstwę hybrydową Ni/Al2O3/ Cgrafit oraz w celach porównawczych warstwę niklową. Jako fazy dyspersyjne stosowano proszki Al2O3 oraz grafitu rozproszone w kąpieli Wattsa. Charakterystykę faz dyspersyjnych realizowano za pomocą skaningowej mikroskopii elektronowej (SEM) oraz spektroskopii Ramana dla proszku grafitu. Przedstawiono wyniki badań struktury oraz składu chemicznego wytworzonych warstw za pomocą SEM z przystawką EDS, wyniki pomiarów twardości metodą Vickersa, a także wyniki badań korozyjnych za pomocą elektrochemicznej metody potencjodynamicznej. Charakterystykę zniszczeń po badaniach korozyjnych dokonano za pomocą mikroskopu świetlnego.

Słowa kluczowe

Keywords

Bibliografia

[1] Dehgahi Shirin, Amini Rasool, Alizadeh Morteza. 2017. "Microstructure and corrosion resistance of Ni-Al2O3-SiC nanocomposite coatings produced by electrodeposition technique". Journal of Alloys and Compounds 692 : 622-628.
[2] Ferrari Andrea. 2007. "Raman spectroscopy of graphene and graphite: Disorder, electron phonon coupling, doping and nonadiabatic effects". Solid State Communications 143: 47-57.
[3] Ferrari Andrea. 2006. "Raman Spectrum of Graphene and Graphene Layers". Physical review letters 97 (18) : id. 187401.
[4]
[4] Gul Haran, Kilic Fatih, Aslan Serdar, A. Alp, Akubult Hatem. 2009. "Characteristics of electro-co-deposited Ni-Al2O3 nano-particle reinforced metal matrix composite (MMC) coatings". Wear 267 : 976-990.
[5] Sasi Arshali, Mondal Manoj, Dayal Saurabh, Kumar Sasi. 2015. "Electro deposition of Nickiel-Alumina Composite Coating". Materials Today: Proceedings 2: 3042-3048.
[6] Sun Wan-chang, Zhang Pei, Zhao Kun, Tian Miao-miao, Wang Ying. 2015. "Effect of graphite concentration on the friction and wear of Ni-Al2O3/graphite composite coatings by a combination of electrophoresis and electrodeposition". Wear 342- 343 : 172-180.
[7] Tang Aigui, Wang Meiling, Huang Wei, Wang Xiaolei. 2015. "Composition design of Ni‑nano-Al2O3-PTFE coatings and their tribological characteristics". Surface & Coatings Technology 282 : 121- 128.
[8] Trzaska Maria, Marta Gostomska. 2009. "Warstwy kompozytowe Ni/Cgrafit wytwarzane metodą elektrochemiczną". Kompozyty 9 (1) : 84- 88.
[9] Wyszyńska Anna, Maria Trzaska. 2004. "Wpływ dyspersyjnej fazy ceramicznej na właściwości niklowych warstw kompozytowych". Kompozyty 4 (9) : 94- 98.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 112186 "Corrosion properties of N..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2018-2 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2018-2

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma